Macro-meso degradation evolution of fully recycled coarse aggregate concrete under sulfate attack in marine environment

被引:1
作者
Jin, Libing [1 ,2 ]
Wu, Tian [1 ]
Liu, Peng [1 ]
Wang, Zhenhao [1 ]
Zhou, Pin [1 ]
机构
[1] Henan Univ Technol, Inst Long Term Performance Concrete Struct, Zhengzhou 450001, Peoples R China
[2] Henan Univ Technol, Design & Res Inst Co Ltd, Zhengzhou 450001, Peoples R China
基金
中国国家自然科学基金;
关键词
Full recycled coarse aggregate concrete; Sulfate attack; Marine engineering; Interfacial transition zone; Mesoscale analysis; MECHANICAL-PROPERTIES; PERFORMANCE; EXPANSION; DAMAGE;
D O I
10.1016/j.istruc.2024.107536
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
External sulfate attack is a major leading cause of early failure of concrete structures in marine environments. In this paper, sulfate erosion experiments were designed and a new mesoscale numerical analysis model was developed,to evaluate the deterioration pattern of sulfate erosion of fully recycled coarse aggregate concrete (FRCAC) in marine environments and promote the application of FRCAC in coastal engineering. A five-phase stochastic convex polygonal aggregate model is developed using a self-programmed program that considers the presence of different types of interfacial transition zones within the FRCAC structure to be closer to the real situation. The concentration distribution pattern of sulfate ions in FRCAC was obtained by exposing the specimens to sodium sulfate solution. The validity and practicality of the mesoscale numerical analysis model were verified by the experimental results. In addition, the evolution regularity of sulfate ions, expansion products, and expansion strains in FRCAC was further investigated by the new numerical modeling. The results can be shown that: the sulfate ion content at the identical depth improved by 21.95 % when the water-cement ratio was increased from 0.4 to 0.6. The sulfate ion content at the same depth grown by about 9 times when the surface sulfate concentration was raised from 1 % to 10 %. When the initial aluminate content was increased up to four times, the production of ettringite increased by about 3 times and the swelling strain approximately increased by 5 times.
引用
收藏
页数:14
相关论文
共 44 条
  • [41] Time-dependent reliability analysis of recycled aggregate concrete cover cracking induced by reinforcement corrosion
    Zhang, Kaijian
    Xiao, Jianzhuang
    Zhang, Qingtian
    [J]. JOURNAL OF BUILDING ENGINEERING, 2021, 39 (39):
  • [42] Three-dimensional reconstruction and sulfate ions transportation of interfacial transition zone in concrete under dry-wet cycles
    Zheng, Suining
    He, Rui
    Chen, Huaxin
    Wang, Zhendi
    Huang, Xin
    Liu, Shaowen
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2021, 291
  • [43] Methods for improving the durability of recycled aggregate concrete: A review
    Zheng, Yuanxun
    Zhang, Yahui
    Zhang, Peng
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 6367 - 6386
  • [44] Numerical investigation on expansive volume strain in concrete subjected to sulfate attack
    Zuo, Xiao-Bao
    Sun, Wei
    Yu, Cheng
    [J]. CONSTRUCTION AND BUILDING MATERIALS, 2012, 36 : 404 - 410