Flow stress of a new type Al-Cu-Li system alloy during hot compression deformation

被引：0

作者：

Key Laboratory of Nonferrous Metal Materials Science and Engineering, Central South University, Changsha 410083, China ^{[1
]}

机构：

来源：

Beijing Keji Daxue Xuebao | 2006年 / 8卷 / 750-754期

关键词：

Activation energy - Deformation - Hot pressing - Lithium alloys - Plastic flow - Strain rate - Temperature;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The flow stress behavior of a new type Al-Cu-Li system alloy during hot compression deformation was studied in the strain rate range from 0.01 to 10s-1 and the temperature range from 300 to 500°C by isothermal compression test on a Gleeble 1500 thermal-mechanical simulator. The results show that the flow stress of this new type Al-Cu-Li system alloy decreases with the increase of deformation temperature and increases with the increase of strain rate. The peak flow stress during high temperature deformation can be represented by Z parameter in a hyperbolic sine function. The analytical expression of peak flow stress was fitted with the hot deformation activation energy of 239.02 kj&middotmol-1.

引用