Corrosion resistance, composition and structure of RE chemical conversion coating on magnesium alloy

被引：0
作者：
Yu, Sheng-Xue [1 ,2 ]
Cao, Jing-Yu [2 ]
Chen, Ling [2 ]
Han, Jing [2 ]
Zhang, Rui-Jun [1 ]
机构：
[1] State Key Laboratory of Metastable Materials Science and Technology, Yanshan University
[2] Department of Applied Chemistry, Yanshan University
来源：
Transactions of Nonferrous Metals Society of China (English Edition) | 2008年 / 18卷 / SPEC. ISSUE 1期
关键词：
Chemical conversion coating; Corrosion resistance; Magnesium alloy; Rare earths;
D O I：
10.1016/s1003-6326(10)60230-0
中图分类号：
学科分类号：
摘要：
Golden yellow rare earths chemical conversion coating was obtained on the surface of magnesium alloy by immersing in cerium sulfate solution. The corrosion resistance of RE conversion coating was evaluated using immersion test and potentiodynamic polarization measurements in 3.5% NaCl solution. The morphologies of samples before corrosion and after corrosion were observed by SEM. The structures and compositions of the RE conversion coating were studied by means of XPS, XRD and IR. The results show that, the conversion coating consists of mainly two kinds of element Ce and O, the valences of cerium are +3 and +4, and OH- exists in the coating. The anti-corrosion property of magnesium alloy is increased obviously by rare earths conversion coating, Its self-corrosion current density decreases and the coating has self-repairing capability in the corrosion process in 3.5% NaCl solution.
引用
收藏
页码：s349 / s353
页数：4
相关论文
共 16 条
  • [1] Liu Z., Wang Y., Wang Z.-G., Li F., Shen Z.-Y., Developing trends of research and application of magnesium alloys, Chinese Journal of Materials Research, 14, 6, pp. 449-456, (2000)
  • [2] Zeng R.-C., Ke W., Xu Y.-B., Recent development and application of magnesium alloys, Actametallurgica Sinica, 37, 7, pp. 673-685, (2001)
  • [3] Zhang C.-X., Chen P.-L., Chen J., Application and research progress of magnesium alloys in automobile industry, Foundry Technology, 29, 4, pp. 531-535, (2008)
  • [4] Xu H.-X., Zhang X.-L., Green enviroment - Friendly materials for 21 century - magnesium alloys, Journal of Shanghai University of Engineering Science, 21, 4, pp. 322-325, (2007)
  • [5] Zhao M., Wu S.-S., An P., Fukuda Y., Nakae H., Growth of multi-elements complex coating on AZ91D magnesium alloy through conversion treatment, Journal of Alloys and Compounds, 427, 1-2, pp. 310-315, (2007)
  • [6] Chen F., Zhou H., Yao B., Qin Z., Zhang Q., Corrosion resistance property of the ceramic coating obtained through microarc oxidation on the AZ31 magnesium alloy surfaces, Surface and Coatings Technology, 201, 9-11 SPEC. ISS, pp. 4905-4908, (2007)
  • [7] Anik M., Korpe E., Effect of alloy microstructure on electroless NiP deposition behavior on Alloy AZ91, Surface and Coatings Technology, 201, 8, pp. 4702-4710, (2007)
  • [8] Zhu L.-Q., Li W.-P., Shan D.-D., Effects of low temperature thermal treatment on zinc and/or tin plated coatings of AZ91D magnesium alloy, Surface and Coatings Technology, 201, 6, pp. 2768-2775, (2006)
  • [9] Jin F.-Y., Chub P.K., Xua G.-D., Zhao J., Tang D.-L., Tong H.-H., Structure and mechanical properties of magnesium alloy treated by micro-arc discharge oxidation using direct current and high-frequency bipolar pulsing modes, Materials Science and Engineering A, 436-446, 5, pp. 123-126, (2006)
  • [10] Shi H.-Y., Yang W., Jiang B.-L., Composite technology and coatings obtained by micro-arc oxidation and electrophoresis of AZ31 Mg-based, Journal of Chinese Society for Corrosion and Protection, 28, 3, pp. 155-160, (2008)
12