A comparison of high temperature corrosion behaviour between uncoated, Ni-Cr-Mo and Ni-Cr-Al-Y coated 316 stainless steel in ZnCl2-KCl environment

被引：0

作者：

Mangaladevi, Pooja ^{[1
]}

Vijeesh, V. ^{[2
]}

Ravishankar, K. S. ^{[3
]}

Madav, Vasudeva ^{[1
]}

机构：

[1] Natl Inst Technol Karnataka, Dept Mech Engn, Mangalore 575025, India

[2] Nitte Deemed Univ, NMAM Inst Technol NMAMIT, Dept Mech Engn, Nitte 574110, India

[3] Natl Inst Technol Karnataka, Dept Met & Mat Engn, Mangalore 575025, India

来源：

RESULTS IN ENGINEERING | 2025年 / 25卷

关键词：

High-temperature corrosion; Stainless steel; Degradation; Molten salt; Coatings; corrosion rate; OXIDATION; COATINGS; PROTECTION; ALLOYS;

D O I：

10.1016/j.rineng.2025.103920

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High-temperature corrosion poses a significant challenge to the longevity and performance of materials in extreme environments. This study investigates the corrosion behavior of coated and uncoated 316 stainless steel (SS) in ZnCl2-KCl eutectic molten salt vapor at 600 degrees C. Contrary to expectations, the results indicate that uncoated 316 SS exhibits lesser corrosion compared to certain coated samples over prolonged exposure. Comprehensive analysis, including weight change measurements, electrochemical evaluations, and surface morphology examination, reveals the degradation mechanisms and the efficacy of coatings. Amongst the various materials used for study, NiCrMo coated 316SS showed least corrosion rate of 8.34 mpy and 3.2 mpy after 20 hand 100 h respectively. The findings provide insights into optimizing material protection strategies in harsh chloride containing molten salt environments.

引用

页数：8

共 24 条

[21] Corrosion behaviors of 316 stainless steel and Inconel 625 alloy in chloride molten salts for solar energy storage [J].

Wang, Mingjing ;

Zeng, Song ;

Zhang, Huihui ;

Zhu, Ming ;

Lei, Chengxin ;

Li, Boshuai .

HIGH TEMPERATURE MATERIALS AND PROCESSES, 2020, 39 (01) :340-350

[22]

Yamamoto S., 2014, Heat-Resistant austenitic stainless steel

[23] Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments [J].

Yeh, Chun-Ping ;

Tsai, Kun-Chao ;

Huang, Jiunn-Yuan .

MATERIALS, 2020, 13 (24) :1-19

[24] Experimental Study of Eutectic Molten Salts NaCl/KCl/ZnCl2 Heat Transfer Inside a Smooth Tube for High-Temperature Application [J].

Zhang, Ye ;

Wang, Xiaoxin ;

Hu, Qichao ;

Li, Peiwen ;

Liu, Qibin ;

Xu, Ben .

JOURNAL OF SOLAR ENERGY ENGINEERING-TRANSACTIONS OF THE ASME, 2022, 144 (04)

← 1 2 3 →