Flow and thermal characteristics of cationic dyeable nylon 6/cationic dyeable poly(ethylene terephthalate) polyblended polymers and filaments

被引：0

作者：

Shu, Yao-Chi ^{[1
]}

Hsiao, Kai-Jen ^{[2
]}

机构：

[1] Department of Polymer Materials, Vanung University, Chungli City, 320, Taiwan

[2] Fiber Technology Division, MCL/ITRI, Hsinchu, 300, Taiwan

来源：

Journal of Applied Polymer Science | 1600年 / 103卷 / 03期

关键词：

Cationic dyeable nylon 6 (CD-N6) and cationic dyeable poly(efhylene terephfhalate) (CD-PET) polymers were extruded (in the proportions of 75/25; 50/50; 25/75) from one melt twin-screw extruders to prepare three CD-N6/CD-PET polyblended polymers and then spin filaments. The molar ratio of 5-sodium sulfonate dimethyl isophthalate (5-SSDMI) for CD-N6 and CD-PET polymers were 2.01% and 2.04%; respectively. This study investigated the flow and thermal characteristics of CD-N6/CD-PET polyblended polymers and filaments using gel permeation chromatography (GPC); differential scanning calorimetry (DSC); thermogravimetric analysis (TGA); potentiometer; a rheometer; the density gradient; wide-angle X-ray diffraction (WAXD); and extension stress-strain measurement. Flow behavior of CD-N6/CD-PET polyblended polymers exhibited negative-deviation blends (NDB); and the 50/50 blend of CD-N6/CD-PET showed a minimum value of the meltviscosity. Experimental results of the DSC indicated CD-N6 and CD-PET molecules formed an immiscible system. Particularly; a double endothermic peak was observed from CD-N6; CD-PET and their polyblended filaments. The tenacity of CD-N6/CD-PET polyblended filaments decreased initially and then increased as the CD-PET content increased. Crystallinities and densities of CD-N6/CD-PET polyblended filaments were the linear relation with the blend ratio. The miscibility parameter μ values of CD-N6/ CD-PET all samples were less than zero. It indicated the electrostatic repulsion was evident between CD-N6 and CD-PET molecules. From the experimental data; the CD-N6 and CD-PET polymers were identified to be immiscible. © 2006 Wiley Periodicals; Inc;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：2049 / 2056