Research on microstructures and mechanical properties of hot rolled Ti-microalloyed TRIP steel

被引:0
|
作者
机构
[1] Yi, Hai-Long
[2] Xu, Wei
[3] Long, Lei-Zhou
[4] Liu, Zhen-Yu
[5] Wang, Guo-Dong
来源
Yi, Hai-Long | 1600年 / Beijing Institute of Aeronautical Materials (BIAM)卷
关键词
Austenite/martensite transformations - Continuous cooling transformation curves - Fine precipitates - Finish rolling temperature - Hot-rolled trip steels - Microstructures and mechanical properties - Retained austenite - Strength and elongations;
D O I
10.11868/j.issn.1001-4381.2014.12.012
中图分类号
学科分类号
摘要
A Ti-microalloyed TRIP steel was selected, and the continuous cooling transformation curve was measured. The microstructures and mechanical properties of steels were investigated at different rolling and cooling processes. The results show that the austenite/ferrite and austenite/martensite transformation temperature are at about 500-650℃ and 450℃, respectively. The microstructure of steel is composed of ferrite/bainite and a small amount of retained austenite. The yield strength and tensile strength of steel decrease with the increasing of finish rolling temperature. The yield strength of steel decreases with the decreasing of air cooling end temperature. When the finish rolling and air cooling end temperature are 796℃ and 722℃, respectively, and the yield strength, tensile strength and the product of strength and elongation of the steel are 661, 888 MPa and 25042 MPa·%, respectively. The microstructure is consisted of fine ferrite and lath bainite, and a large number of fine precipitates presents on the ferrite matrix. ©, 2014, Beijing Institute of Aeronautical Materials (BIAM). All right reserved.
引用
收藏
相关论文
共 50 条
  • [2] Development of Ti-Microalloyed 600 MPa hot rolled high strength steel
    Hai-long Yi
    Zhen-yu Liu
    Guo-dong Wang
    Di Wu
    Journal of Iron and Steel Research International, 2010, 17 : 54 - 58
  • [3] Development of Ti-Microalloyed 600 MPa Hot Rolled High Strength Steel
    Yi Hai-long
    Liu Zhen-yu
    Wang Guo-dong
    Wu Di
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2010, 17 (12) : 54 - 64
  • [4] Mechanical Properties of TRIP Steel Microalloyed with Ti
    Daniel Krizan
    Bruno C. De Cooman
    Metallurgical and Materials Transactions A, 2014, 45 : 3481 - 3492
  • [5] Mechanical Properties of TRIP Steel Microalloyed with Ti
    Krizan, Daniel
    De Cooman, Bruno C.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (08): : 3481 - 3492
  • [6] Microstructure and properties of Ti-microalloyed steel
    Khalid, FA
    Khan, MA
    FUNDAMENTALS AND APPLICATIONS OF MICROALLOYING FORGING STEELS, 1996, : 187 - 194
  • [8] Transformation of Ti-microalloyed TRIP steel during continuous cooling
    Yi, Hai-Long
    Xu, Wei
    Long, Lei-Zhou
    Liu, Zhen-Yu
    Cailiao Gongcheng/Journal of Materials Engineering, 2015, 43 (03): : 7 - 11
  • [10] Microstructures and mechanical properties of Nb-Ti bearing hot-rolled TRIP steels
    Chen, Yu
    Tang, Guoyi
    Tian, Haoyang
    Li, Feipeng
    Zhang, Yu
    Wang, Lihui
    Deng, Zhaojun
    Luo, Dexing
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2006, 22 (06) : 759 - 762