Effect of the delignification of wood fibers on the mechanical properties of wood fiber-polypropylene composites

被引：0
|
作者：
Karimi, Alinaghi [1 ]
Nazari, Saleh [1 ]
Ghasemi, Ismaeil [2 ]
Tajvidi, Mehdi [1 ]
Ebrahimi, Ghanbar [1 ]
机构：
[1] Department of Wood and Paper Science and Technology, College of Natural Resources, University of Tehran, Iran
[2] Iran Polymer and Petrochemical Research Institute, Iran
来源：
Journal of Applied Polymer Science | 2006年 / 102卷 / 05期
关键词：
The effect of the delignification of hornbeam fibers on the mechanical properties of wood fiber-polypropylene (PP) composites was studied. Original fibers and delignified fibers at three levels of delignification were mixed with PP at a weight ratio of 40:60 in an internal mixer. Maleic anhydride (0.5 wt %) as the coupling agent and dicumyl peroxide (0.1 wt%) as the initiator were applied. The produced composites were then hot-pressed; and specimens for physical and mechanical testing were prepared. The results of the properties of the composite materials indicate that delignified fibers showed better performance in the enhancement of tensile strength and tensile modulus; whereas the hardness of the composites was unaffected by delignification. Delignified fibers also exhibited better water absorption resistance. Notched impact strength was higher for delignified fiber composites; but it was reduced at higher delignification levels. © 2006 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：4759 / 4763
相关论文
共 50 条
  • [41] The effect of chemical modification of wood in ionic liquids on the supermolecular structure and mechanical properties of wood/polypropylene composites
    Borysiak, Slawomir
    Grzabka-Zasadzinska, Aleksandra
    Odalanowska, Majka
    Skrzypczak, Andrzej
    Ratajczak, Izabela
    CELLULOSE, 2018, 25 (08) : 4639 - 4652
  • [42] The effect of chemical modification of wood in ionic liquids on the supermolecular structure and mechanical properties of wood/polypropylene composites
    Slawomir Borysiak
    Aleksandra Grząbka-Zasadzińska
    Majka Odalanowska
    Andrzej Skrzypczak
    Izabela Ratajczak
    Cellulose, 2018, 25 : 4639 - 4652
  • [43] Some microwave and mechanical properties of carbon fiber-polypropylene and carbon black-polypropylene composites
    Kaynak, A
    Polat, A
    Yilmazer, U
    MATERIALS RESEARCH BULLETIN, 1996, 31 (10) : 1195 - 1206
  • [44] Polypropylene composites with natural fibers and wood - General mechanical property profiles
    Sobczak, Lukas
    Lang, Reinhold W.
    Haider, Andreas
    COMPOSITES SCIENCE AND TECHNOLOGY, 2012, 72 (05) : 550 - 557
  • [45] Effect of repeated cycles of wetting and drying on mechanical properties of wood–polypropylene composites
    Jayashri Gunjal
    R. M. Abhilash
    Shakti Singh Chauhan
    Journal of the Indian Academy of Wood Science, 2020, 17 : 114 - 122
  • [46] Mechanical Properties of Wood Flour Polypropylene Composites: Effect of Cycled Temperature Change
    Lee, S. Y.
    Chun, S. J.
    Doh, G. H.
    Park, S. B.
    Choi, S., I
    ELASTOMERS AND COMPOSITES, 2011, 46 (03): : 218 - 222
  • [47] Influence of Wood Species and Particle Size on Mechanical and Thermal Properties of Wood Polypropylene Composites
    Ratanawilai, Thanate
    Nakawirot, Kamonchanok
    Deachsrijan, Arsiwan
    Homkhiew, Chatree
    FIBERS AND POLYMERS, 2014, 15 (10) : 2160 - 2168
  • [48] MECHANICAL PROPERTIES OF WOOD-POLYPROPYLENE COMPOSITES WITH INDUSTRIAL WOOD PARTICLES OF DIFFERENT SIZES
    Gozdecki, Cezary
    Wilczynski, Arnold
    Kociszewski, Marek
    Tomaszewska, Jolanta
    Zajchowski, Stanislaw
    WOOD AND FIBER SCIENCE, 2012, 44 (01): : 14 - 21
  • [49] The effect of lignin as a compatibilizer on the physical properties of coconut fiber-polypropylene composites
    Rozman, HD
    Tan, KW
    Kumar, RN
    Abubakar, A
    Ishak, ZAM
    Ismail, H
    EUROPEAN POLYMER JOURNAL, 2000, 36 (07) : 1483 - 1494
  • [50] Orange Wood Fiber Reinforced Polypropylene Composites: Thermal Properties
    Reixach, Rafel
    Puig, Josep
    Alberto Mendez, Jose
    Girones, Jordi
    Espinach, Francesc X.
    Arbat, Gerard
    Mutje, Pere
    BIORESOURCES, 2015, 10 (02): : 2156 - 2166
12345