Surface modification of polyester and polyamide fabrics by low frequency plasma polymerization of acrylic acid

被引：0
|
作者：
Cireli, Aysun [1 ]
Kutlu, Bengi [1 ]
Mutlu, Mehmet [2 ]
机构：
[1] Textile Engineering Department, Faculty of Engineering, Dokuz Eylul University, Izmir, Turkey
[2] Plasma Aided Biotechnology and Bioengineering Research Group (PABB), Faculty of Engineering, Hacettepe University, Ankara, Turkey
来源：
Journal of Applied Polymer Science | 2007年 / 104卷 / 04期
关键词：
In this study; the surface characteristics of polyester and polyamide fabrics were changed by plasma polymerization technique utilizing acrylic acid as precursor. This monomer was used to produce hydrophilic materials with extended absorbency. The hydrophilicity; total wrinkle recovery angle (WRA°) and breaking strength of the fabrics were determined prior and after plasma polymerization treatment. The modification of surfaces was carried out at low pressure (<100 Pa) and low temperature (<50°C) plasma conditions. The effects of exposure time and discharge power parameters were optimized by comparing properties of the fabrics before and after plasma polymerization treatments. It was shown that two sides of polyester fabric samples were treated equally and homogeneously in plasma reactor. For polyester fabrics; the minimum wetting time; 0.5; s; was observed at two plasma processing parameters of 10 W-45 min and 10 W-20 min; where untreated fabric has a wetting time of 6 s. For polyester fabrics; the maximum value was obtained at 60 W-5 min with the wrinkle recovery angle of 306° where the untreated fabric has 290°. The optimum plasma conditions for polyamide fabrics were determined as 30 W-45 min where 2 s wetting time was observed. Wrinkle recovery angle of untreated polyamide fabric was 264°. In this study; after plasma polymerization of acrylic acid; wrinkle recovery angle values were increased by 13%. No significant change was observed in breaking strength of both fabrics after plasma treatment. © 2007 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：2318 / 2322
相关论文
共 50 条
  • [31] Polyester and Polyamide Fiber Modification by Cold Plasma Activation.
    Bogoeva-Gaceva, Gordana
    Lozinski, Dimitrije
    Petrov, Duro
    Polimeri (Zagreb), 1986, 7 (4-5): : 103 - 104
  • [32] Modification of polysulfone membranes. 2. Plasma grafting and plasma polymerization of acrylic acid
    Gancarz, I
    Pozniak, G
    Bryjak, M
    Frankiewicz, A
    ACTA POLYMERICA, 1999, 50 (09) : 317 - 326
  • [33] Acrylic acid plasma polymerization to modify the surface of expanded poly(tetrafluoroethylene).
    Chen-Yang, YW
    Chen, CW
    Tseng, SC
    Wu, YZ
    Yang, HC
    Kau, JY
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2003, 226 : U368 - U368
  • [34] Plasma Polymerization of Acrylic Acid Revisited
    Hegemann, Dirk
    Koerner, Enrico
    Guimond, Sebastien
    PLASMA PROCESSES AND POLYMERS, 2009, 6 (04) : 246 - 254
  • [35] Highly effective surface modification using plasma technologies toward green coloration of polyester fabrics
    Fatma Abdelghaffar
    Rehab A. Abdelghaffar
    Usama M. Rashed
    Hend M. Ahmed
    Environmental Science and Pollution Research, 2020, 27 : 28949 - 28961
  • [36] Highly effective surface modification using plasma technologies toward green coloration of polyester fabrics
    Abdelghaffar, Fatma
    Abdelghaffar, Rehab A.
    Rashed, Usama M.
    Ahmed, Hend M.
    ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH, 2020, 27 (23) : 28949 - 28961
  • [37] Surface photochemical graft polymerization of acrylic acid onto polyamide thin film composite membranes
    Thu Hong Anh Ngo
    Tran, D. T.
    Cuong Hung Dinh
    JOURNAL OF APPLIED POLYMER SCIENCE, 2017, 134 (05)
  • [38] Effects of gas composition during plasma modification of polyester fabrics
    Costa, THC
    Feitor, MC
    Alves, C
    Freire, PB
    de Bezerra, CM
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 173 (01) : 40 - 43
  • [39] SURFACE MODIFICATION OF POLYLACTIC ACID FABRICS USING AMBIENT AIR PLASMA
    Skacelova, Dana
    Rapcova, Eliska
    Kovacik, Dusan
    15TH INTERNATIONAL CONFERENCE ON NANOMATERIALS-RESEARCH & APPLICATION, NANOCON 2023, 2024, : 327 - 332
  • [40] Surface modification of polyester fabrics for inkjet printing with atmospheric-pressure air/Ar plasma
    Zhang, Chunming
    Fang, Kuanjun
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (14): : 2058 - 2063
12345