Surface modification of polyester and polyamide fabrics by low frequency plasma polymerization of acrylic acid

被引：0
|
作者：
Cireli, Aysun [1 ]
Kutlu, Bengi [1 ]
Mutlu, Mehmet [2 ]
机构：
[1] Textile Engineering Department, Faculty of Engineering, Dokuz Eylul University, Izmir, Turkey
[2] Plasma Aided Biotechnology and Bioengineering Research Group (PABB), Faculty of Engineering, Hacettepe University, Ankara, Turkey
来源：
Journal of Applied Polymer Science | 2007年 / 104卷 / 04期
关键词：
In this study; the surface characteristics of polyester and polyamide fabrics were changed by plasma polymerization technique utilizing acrylic acid as precursor. This monomer was used to produce hydrophilic materials with extended absorbency. The hydrophilicity; total wrinkle recovery angle (WRA°) and breaking strength of the fabrics were determined prior and after plasma polymerization treatment. The modification of surfaces was carried out at low pressure (<100 Pa) and low temperature (<50°C) plasma conditions. The effects of exposure time and discharge power parameters were optimized by comparing properties of the fabrics before and after plasma polymerization treatments. It was shown that two sides of polyester fabric samples were treated equally and homogeneously in plasma reactor. For polyester fabrics; the minimum wetting time; 0.5; s; was observed at two plasma processing parameters of 10 W-45 min and 10 W-20 min; where untreated fabric has a wetting time of 6 s. For polyester fabrics; the maximum value was obtained at 60 W-5 min with the wrinkle recovery angle of 306° where the untreated fabric has 290°. The optimum plasma conditions for polyamide fabrics were determined as 30 W-45 min where 2 s wetting time was observed. Wrinkle recovery angle of untreated polyamide fabric was 264°. In this study; after plasma polymerization of acrylic acid; wrinkle recovery angle values were increased by 13%. No significant change was observed in breaking strength of both fabrics after plasma treatment. © 2007 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：2318 / 2322
相关论文
共 50 条
  • [1] Surface modification of polyester and polyamide fabrics by low frequency plasma polymerization of acrylic acid
    Cireli, Aysun
    Kutlu, Bengi
    Mutiu, Mehmet
    JOURNAL OF APPLIED POLYMER SCIENCE, 2007, 104 (04) : 2318 - 2322
  • [2] Modification of polyester and polyamide fabrics by different in situ plasma polymerization methods
    Öktem, T
    Seventekin, N
    Ayhan, H
    Piskin, E
    TURKISH JOURNAL OF CHEMISTRY, 2000, 24 (03): : 275 - 285
  • [3] Modification of polyester fabrics by in situ plasma or post-plasma polymerisation of acrylic acid
    Öktem, T
    Ayhan, H
    Seventekin, N
    Piskin, E
    JOURNAL OF THE SOCIETY OF DYERS AND COLOURISTS, 1999, 115 (09): : 274 - 279
  • [4] Surface modification and characterization of cotton and polyamide fabrics by plasma polymerization of hexamethyldisilane and hexamethyldisiloxane
    Kilic, Bengi
    Aksit, Aysun Cireli
    Mutlu, Mehmet
    INTERNATIONAL JOURNAL OF CLOTHING SCIENCE AND TECHNOLOGY, 2009, 21 (2-3) : 137 - 145
  • [5] Surface Modification of Polyamide Ultrafiltration Membrane by Plasma Polymerisation of Acrylic Acid
    Suhaimi, A.
    Mahmoudi, E.
    Siow, K. S.
    Wee, M. F. Mohd Razip
    SAINS MALAYSIANA, 2020, 49 (12): : 3097 - 3104
  • [6] Surface Modification of Textiles by Glow Discharge Technique: Part II: Low Frequency Plasma Treatment of Wool Fabrics with Acrylic Acid
    Kutlu, Bengi
    Aksit, Aysun
    Mutlu, Mehmet
    JOURNAL OF APPLIED POLYMER SCIENCE, 2010, 116 (03) : 1545 - 1551
  • [7] Investigation the surface modification of Polyamide fabrics using Low-Pressure Plasma Technique
    Hassan, Zuhaib
    Atalay, Ozgur
    Kalaoglu, Fatma
    18TH WORLD TEXTILE CONFERENCE (AUTEX 2018), 2018, 460
  • [8] Effect of low-temperature plasma treatment on surface modification of cotton and polyester fabrics
    Rashidi, A
    Moussavipourgharbi, H
    Mirjalili, M
    Ghoranneviss, M
    INDIAN JOURNAL OF FIBRE & TEXTILE RESEARCH, 2004, 29 (01) : 74 - 78
  • [9] Surface modification of polyamide TFC membranes via redox-initiated graft polymerization of acrylic acid
    Thu Hong Anh Ngo
    Khai Dinh Do
    Dung Thi Tran
    JOURNAL OF APPLIED POLYMER SCIENCE, 2017, 134 (29)
  • [10] Surface modification of TiO2 nanoparticles through plasma polymerization of acrylic acid
    Zhu, Feng
    Kong, Eric Siu-Wai
    Zhang, Jing
    Zhang, Yafei
    CHEMICAL PHYSICS LETTERS, 2006, 423 (4-6) : 270 - 275
12345