Properties of dispersion casting of Y2O3 particles in hypo, hyper and eutectic binary Al-Cu alloys

被引:0
作者
Nuclear Nano-Materials Development Lab., Korea Atomic Energy Research Institute , 150 Deukjin-dong, Yuseong-gu, Daejeon, Korea, Republic of [1 ]
机构
来源
J Mater Sci Technol | 2008年 / 1卷 / 57-59期
关键词
Aluminum copper alloys - Casting - Dispersions - Particles (particulate matter);
D O I
暂无
中图分类号
学科分类号
摘要
In the present work, the dispersion casting of Y2O3 particles in aluminum-copper alloy was investigated in terms of microstructural changes with respect to Cu contents of 20 (hypo), 33 (eutectic) and 40 (hyper) wt pct by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). For the fabrication of Al-Cu alloy dispersed Y2O3 ceramic particles, stir casting method was employed. In case of Al-20 wt pct Cu alloy (hypoeutectic), SEM images revealed that primary Al was grown up in the beginning. After that, eutectic phase with well dispersed ceramic particles was formed. In case of eutectic composition, Y2O3 particles were uniformly dispersed in the matrix. When the Cu is added into Al up to 40 wt pct (hypereutectic), primary θ phase was grown up without any Y2O3 ceramic particles in the early stage of solidification. Thereafter, eutectic phase was formed with well dispersed ceramic particles. It can be concluded that Y2O3 ceramic particles is mostly dispersed in case of eutectic composition in Al-Cu alloy.
引用
收藏
相关论文
共 50 条
  • [31] BEHAVIOR OF Y2O3 AND Al2O3 PARTICLES NEAR THE SOLIDIFICATION FRONT
    Zak, Pawel L.
    Kalisz, Dorota
    Raczkowski, Grzegorz
    METAL 2017: 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2017, : 267 - 272
  • [32] Interface interaction and wetting in the Y2O3/(Al-Cu-Y) system
    Barzilai, S.
    Aizenshtein, M.
    Shapiro-Tsoref, E.
    Froumin, N.
    Frage, N.
    International Journal of Adhesion and Adhesives, 2007, 27 (05): : 358 - 361
  • [33] Interface interaction and wetting in the Y2O3/(Al-Cu-Y) system
    Barzilai, S.
    Alzenshtein, M.
    Shapiro-Tsoref, E.
    Froumin, N.
    Frage, N.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2007, 27 (05) : 358 - 361
  • [34] MICROSTRUCTURE, CORROSION AND WEAR BEHAVIOUR OF UFG-POWDER-METALLURGICAL Al-Cu ALLOYS, Al-Cu/Al2O3(p) AND Al-Cu/SiC(p) COMPOSITES
    Nickel, D.
    Alisch, G.
    Podlesak, H.
    Hockauf, M.
    Fritsche, G.
    Lampke, T.
    REVIEWS ON ADVANCED MATERIALS SCIENCE, 2010, 25 (03) : 261 - 269
  • [35] Dispersion of SiC in aqueous media with Al2O3 and Y2O3 as sintering additives
    Zhang, JX
    Iwasa, M
    Jiang, DL
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (04) : 1013 - 1016
  • [36] BENEFICIAL-EFFECTS OF Y2O3 DISPERSION ON AL2O3 PROTECTIVE COATING
    IKEDA, Y
    YATA, M
    JOURNAL DE PHYSIQUE IV, 1993, 3 (C9): : 257 - 264
  • [37] Slip-casting properties of Si3N4 with Y2O3 and Al2O3 as sintering additives
    U. Senturk
    M. Timucin
    Journal of Materials Science, 1998, 33 : 1881 - 1885
  • [38] Mechanical properties of tungsten alloys with Y2O3 and titanium additions
    Aguirre, M. V.
    Martin, A.
    Pastor, J. Y.
    LLorca, J.
    Monge, M. A.
    Pareja, R.
    JOURNAL OF NUCLEAR MATERIALS, 2011, 417 (1-3) : 516 - 519
  • [39] Slip-casting properties of Si3N4 with Y2O3 and Al2O3 as sintering additives
    Senturk, U
    Timucin, M
    JOURNAL OF MATERIALS SCIENCE, 1998, 33 (07) : 1881 - 1885
  • [40] Powder metallurgical fabrication of SiC and Al2O3 reinforced Al-Cu alloys
    Podlesak, H.
    Siebeck, S.
    Muecklich, S.
    Hockauf, M.
    Meyer, L. W.
    Wielage, B.
    Weber, D.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2009, 40 (07) : 500 - 505