Influence of MC Carbides on Pitting Corrosion Resistance of Weld Metal in Austenitic Stainless Steels

被引：0

作者：

Kadoi, Kota ^{[1
]}

Kanno, Yudai ^{[2
,3
]}

Aoki, So ^{[4
]}

Inoue, Hiroshige ^{[1
]}

机构：

[1] Osaka Univ, Joining & Welding Res Inst, 11-1 Mihogaoka, Ibaraki, Osaka 5670047, Japan

[2] Osaka Univ, Grad Sch Engn, 1 Kokan Cho, Fukuyama, Hiroshima 7210931, Japan

[3] JFE Steel, 1 Kokan Cho, Fukuyama, Hiroshima 7210931, Japan

[4] Japan Atom Energy Agcy, 2-4 Shirakata, Tokai, Ibaraki 3191195, Japan

来源：

ISIJ INTERNATIONAL | 2024年 / 64卷 / 09期

关键词：

pitting corrosion; weld metal; Cr depletion; stainless steel; sensitization; carbide; BEHAVIOR; SOLIDIFICATION; MICROSTRUCTURE; TEMPERATURE; WELDABILITY; NIOBIUM; JOINTS;

D O I：

10.2355/isijinternational.ISIJINT-2024-067

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The influence of MC-type carbide formation on pitting corrosion resistance in weld metal of austenitic stainless steel was investigated. The relationship between the microstructure such as carbides and element distribution, and pitting corrosion resistance of the simulated weld metal of austenitic stainless steel was studied. The addition of molybdenum improved the pitting corrosion resistance. The effect of niobium addition on the pitting resistance was negligible. However, the addition of titanium significantly reduced the pitting corrosion resistance. The addition of niobium or titanium induced the formation of MC-type carbides, such as TiC and NbC, at the cellular boundaries. The pits were mainly initiated near or at carbides. The chromium depletion zone was formed near M23C6 coexisting with TiC only in the specimen added titanium. Thus, TiC formed during solidification accelerated the chromium diffusion-associated M23C6 precipitation on TiC. The depletion zone deteriorated the pitting corrosion resistance of the titanium-containing specimen.

引用

页码：1450 / 1456

页数：7

共 50 条

[41] Effects of surface preparation on pitting resistance, residual stress, and stress corrosion cracking in austenitic stainless steels
Ben Rhouma, A
Braham, C
Fitzpatrick, ME
Lédion, J
Sidhom, H
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2001, 10 (05) : 507 - 514
[42] Eliminating detrimental effect of cold working on pitting corrosion resistance in high nitrogen austenitic stainless steels
Wang, Qingchuan
Zhang, Bingchun
Ren, Yibin
Yang, Ke
CORROSION SCIENCE, 2017, 123 : 351 - 355
[43] INFLUENCE OF PROCESS PARAMETERS ON THE CORROSION RESISTANCE OF CORRUGATED AUSTENITIC AND DUPLEX STAINLESS STEELS
Alvarez, Sandra M.
Bautista, Asuncion
Velasco, Francisco
MATERIALI IN TEHNOLOGIJE, 2013, 47 (03): : 317 - 321
[44] WELD FUSION LINE CORROSION OF STABILIZED AUSTENITIC STAINLESS-STEELS
CIHAL, V
LOBL, K
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (05) : 418 - 423
[45] AUSTENITIC STAINLESS STEELS WITH HIGH RESISTANCE TO STRESS CORROSION
FERREE, JA
JOURNAL OF METALS, 1968, 20 (08): : A25 - &
[46] EFFECTS OF ALLOYING ELEMENTS ON THE PITTING RESISTANCE OF AUSTENITIC STAINLESS-STEELS
YAMAMOTO, T
AIZAWA, T
HONKURA, Y
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (03) : B68 - B68
[47] Influence of metallurgical and chemical variables on the pitting corrosion behaviour of nitrogen-bearing austenitic stainless steels
Kamachi Mudali, U.
Ningshen, S.
Tyagi, A.K.
Dayal, R.K.
Materials Science Forum, 1999, 318 : 495 - 502
[48] NOTE ON INFLUENCE OF NITROGEN-CONTENT ON RESISTANCE TO PITTING CORROSION OF STAINLESS-STEELS
TRUMAN, JE
COLEMAN, MJ
PIRT, KR
BRITISH CORROSION JOURNAL, 1977, 12 (04): : 236 - 238
[49] The effect of Hydrogen on Pitting Corrosion of Superaustenitic and Austenitic-Ferritic Stainless Steels
Michalska, Joanna
DIFFUSION IN SOLIDS AND LIQUIDS VII, 2012, 326-328 : 620 - 625
[50] EFFECT OF AUTOGENOUS WELDING ON CHLORIDE PITTING CORROSION IN AUSTENITIC STAINLESS-STEELS
GARNER, A
CORROSION, 1979, 35 (03) : 108 - 114

← 1 2 3 4 5 →