Influence of acid pickling on electrodeposition of aluminum on magnesium alloy in room temperature molten salts

被引:0
|
作者
Qian, Hong-Mei [1 ]
Li, Yan [1 ]
Ling, Guo-Ping [1 ]
机构
[1] College of Materials Science and Chemical Engineering, Zhejiang University, Hangzhou 310027, China
来源
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2009年 / 19卷 / 05期
关键词
Adhesion - Aluminum alloys - Corrosion resistant coatings - Seawater corrosion - Corrosion resistance - Atmospheric corrosion - Electrodes - Aluminum corrosion - Electrodeposition - Magnesium alloys - Corrosion resistant alloys;
D O I
暂无
中图分类号
学科分类号
摘要
The effects of different acid pickling processes on the adhesions between the AZ91D magnesium alloy substrate and aluminum coatings electrodeposited from the acid AlCl3-EMIC room temperature molten salts were studied. The adhesions were estimated by score-tearing test. The surface morphology, phase compositions and element valence of coatings/etched substrate were analyzed by OM, SEM, EDS, XRD and XPS. The corrosion resistance was tested by salt-spray. The formation mechanism of coating morphologies was also discussed. The results show that the aluminum coating is not dense and the adhesion between the coatings and substrate is not good after mechanical pretreatment on AZ91D substrate. The dense and uniform coatings can be electrodeposited on the AZ91D substrate after pretreated by hydrofluoric acid pickling. The density of coatings and the adhesion can be improved simultaneously by using diluted phosphoric acid as pickling solution, and thus, the coating provides good protection to the substrate.
引用
收藏
页码:854 / 860
相关论文
共 50 条
  • [31] Preparation of aluminum-tin alloy by electrodeposition in low-temperature molten salt system
    Kan, Hong-min
    Wang, Wen-xin
    Kong, Ling-ming
    Wu, Jiang
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2024, 31 (03) : 783 - 795
  • [32] Coalescence behavior of aluminum alloy drops in molten salts
    Roy, RR
    Sahai, Y
    MATERIALS TRANSACTIONS JIM, 1997, 38 (11): : 995 - 1003
  • [33] Electrodeposition of aluminum-carbon nanotube composite from room-temperature molten salt electrolyte
    Yatsushiro, N
    Koura, N
    Nakano, S
    Ui, K
    Takeuchi, K
    ELECTROCHEMISTRY, 2006, 74 (03) : 233 - 236
  • [34] Electrodeposition of copper and copper-aluminum alloys from a room-temperature chloroaluminate molten salt
    Tierney, BJ
    Pitner, WR
    Mitchell, JA
    Hussey, CL
    Stafford, GR
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (09) : 3110 - 3116
  • [35] ALLOY FORMATION IN ELECTRODEPOSITION OF CHROMIUM ON NIOBIUM CATHODE IN MOLTEN-SALTS
    KUZNETSOV, SA
    GLAGOLEVSKAYA, AL
    RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 1993, 66 (09) : 1615 - 1616
  • [36] ELECTRODEPOSITION OF TANTALUM NIOBIUM ALLOY FROM THE MOLTEN FLUORIDE SALTS BATH
    PAN, SK
    THOMPSON, J
    CAPSIMALIS, GP
    PLATING AND SURFACE FINISHING, 1987, 74 (02): : 44 - 44
  • [37] Room temperature molten salts as lithium battery electrolyte
    Garcia, B
    Lavallée, S
    Perron, G
    Michot, C
    Armand, M
    ELECTROCHIMICA ACTA, 2004, 49 (26) : 4583 - 4588
  • [38] Influence of inorganic acid pickling on the corrosion resistance of magnesium alloy AZ31 sheet
    Nwaogu, U. C.
    Blawert, C.
    Scharnagl, N.
    Dietzel, W.
    Kainer, K. U.
    CORROSION SCIENCE, 2009, 51 (11) : 2544 - 2556
  • [39] Polymer extractions by room temperature chloroaluminate molten salts
    Wilkes, JS
    Castle, PJ
    Schoske, R
    Humphrey, CJ
    Layo, FB
    Slanger, R
    MOLTEN SALTS XII, PROCEEDINGS, 2000, 99 (41): : 65 - 73
  • [40] THE ELECTRODEPOSITION OF ALUMINUM FROM NONAQUEOUS SOLUTIONS AT ROOM TEMPERATURE
    HURLEY, FH
    WIER, TP
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1951, 98 (05) : 207 - 212