Low temperature effect on magnetic conversion and giant magnetoresistance in electrodeposited CoCu/Cu multilayers

被引：0
|
作者：
机构：
[1] Ghosh, S.K.
[2] Dogra, Anjana
[3] Chowdhury, P.
[4] Rajak, S.
[5] Srivastava, C.
来源：
Ghosh, S.K. (sghosh@barc.gov.in) | 1600年 / Elsevier Ltd卷 / 647期
关键词：
Abstract In the present study; the variation of superparamagnetic (SPM) and ferromagnetic (FM) components and their effect on giant magnetoresistance (GMR) in electrodeposited CoCu/Cu multilayers (ML's) were investigated in the temperature range 30-300 K. For this; two different kinds of ML's; one with discontinuous Co-layer consisting of large superparamagnetic (SPM) (tCo = 0.2 and 0.3 nm) fractions and the other with continuous Co-layer containing large ferromagnetic (FM) (tCo = 2 and 3 nm) content were considered. Magnetoresistance measurements showed increase in MR magnitude with decrease in temperature associated with magnetic conversions in the magnetic Co-layers. At 300 K; a substantial difference in magnitude of MR was found for multilayers with tCo = 0.3 (5.07%) and 3 nm (8.82%). However; at 30 K very close values of MR for multilayer pair with tCo = 0.3 (16.48%) and 3 nm (17.72%) ensures a significant transformations of SPM to FM fractions in Co-layer at tCo = 0.3 nm. Similar results were obtained for the other pair of ML's i.e. tCo = 0.2 and 2 nm. This study suggests a suitable minimization of SPM content in the Co-layer could be another effective mechanism in maximizing the MR value. The measured temperature dependence of MR obeyed a simple T1 law. © 2015 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [31] Giant magnetoresistance (GMR) behavior of electrodeposited NiFe/Cu multilayers: Dependence of non-magnetic and magnetic layer thicknesses
    Kuru, Hilal
    Kockar, Hakan
    Alper, Mursel
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2017, 444 : 132 - 139
  • [32] Structural evolution during growth of electrodeposited Co-Cu/Cu multilayers with giant magnetoresistance
    Cziráki, A
    Péter, L
    Arnold, B
    Thomas, J
    Bauer, HD
    Wetzig, K
    Bakonyi, I
    THIN SOLID FILMS, 2003, 424 (02) : 229 - 238
  • [33] Correlation between interface structure and giant magnetoresistance in electrodeposited Co-Cu/Cu multilayers
    Cziráki, A
    Köteles, M
    Péter, L
    Kupay, Z
    Pádár, J
    Pogány, L
    Bakonyi, I
    Uhlemann, M
    Herrich, M
    Arnold, B
    Thomas, J
    Bauer, HD
    Wetzig, K
    THIN SOLID FILMS, 2003, 433 (1-2) : 237 - 242
  • [34] Asymmetric giant magnetoresistance effect in Py/Cu multilayers
    Lucinski, T
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2000, 219 (03) : 303 - 308
  • [35] Giant magnetoresistance in electrodeposited Co-Cu/Cu multilayers: Origin of the absence of oscillatory behavior
    Bakonyi, I.
    Simon, E.
    Toth, B. G.
    Peter, L.
    Kiss, L. F.
    PHYSICAL REVIEW B, 2009, 79 (17)
  • [36] Giant magnetoresistance in magnetic multilayers
    Reiss, G.
    Koch, M.
    Brueckl, H.
    Von Loyen, L.
    Wissenschaftlinche Zeitschrift der Technischen Universitat Dresden, 46 (03):
  • [37] The giant magnetoresistance of magnetic multilayers
    Van Dau, FN
    VIDE-SCIENCE TECHNIQUE ET APPLICATIONS, 1998, 53 (290): : 770 - +
  • [38] Study of strain and giant magnetoresistance of Co/Cu magnetic multilayers
    Suenaga, Kazufumi
    Oomi, Gendo
    Uwatoko, Yoshiya
    Saito, Kesami
    Takanashi, Koki
    Fujimori, Hiroyasu
    JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN, 2006, 75 (07)
  • [39] High magnetoresistance and low coercivity in electrodeposited Co/Cu granular multilayers
    Ghosh, S. K.
    Grover, A. K.
    Chowdhury, P.
    Gupta, S. K.
    Ravikumar, G.
    Aswal, D. K.
    Kumar, M. Senthil
    Dusane, R. O.
    APPLIED PHYSICS LETTERS, 2006, 89 (13)
  • [40] GIANT MAGNETORESISTANCE IN SOFT-MAGNETIC NIFECO/CU MULTILAYERS
    JIMBO, M
    TSUNASHIMA, S
    KANDA, T
    GOTO, S
    UCHIYAMA, S
    JOURNAL OF APPLIED PHYSICS, 1993, 74 (05) : 3341 - 3344
12345