Cracking Failure Analysis of a 2205 Duplex Stainless Steel Elbow in a Natural Gas Treatment Station

被引:0
|
作者
Song, Chengli [1 ,2 ,3 ]
Song, Wenwen [4 ]
Ma, Chao [4 ]
Luo, Jinheng [1 ,2 ]
Li, Lifeng [1 ,2 ]
机构
[1] State Key Lab Oil & Gas Equipment, Xian 710077, Peoples R China
[2] CNPC Tubular Goods Res Inst, Xian 710077, Peoples R China
[3] Xian Shiyou Univ, Xian 710065, Shaanxi, Peoples R China
[4] PetroChina Tarim Oilfield Co, Koral 841000, Xinjiang, Peoples R China
关键词
Elbow; Crack; Decarbonization; Failure; DECARBURIZATION;
D O I
10.1007/s11668-024-02076-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A leakage accident occurred in an elbow of a natural gas processing station in western China. In order to analyze the cause of the accident, non-destructive testing, chemical composition analysis, hardness testing, metallographic examination, scanning electron microscopy analysis and other experimental analyses were carried out on the elbow. The obtained results showed that the present leakage is mainly attributed to the cracks. In fact, the microstructure around the cracks was decarburized which fully indicates that the cracks have experienced a high temperature environment. In other words, the elbow had formed initial cracks before the heat treatment process of manufacturing. Then, the cracks grew until they penetrated the wall thickness under the action of working pressure. In addition, considering that the material properties test results of the elbow meet the standard requirements, and there are no H2S, H2 and other media that cause SSC and HIC in the service environment, it is once again confirmed that the failure of the elbow is caused by defects in the original manufacturing stage. It is recommended that the same batch of elbows in service to carry out internal and external defects, and strengthen the quality inspection of the new elbows, to avoid defective elbows in the field to put into use.
引用
收藏
页码:2871 / 2878
页数:8
相关论文
共 50 条
  • [31] Influence of ageing treatment on microstructures and mechanical properties of 2205 duplex stainless steel
    Wu T.-H.
    Liu C.-M.
    Jiang Z.-H.
    Fan G.-W.
    Dongbei Daxue Xuebao, 9 (1317-1321): : 1317 - 1321
  • [32] Hot Deformation Behavior of Duplex Stainless Steel 2205
    Zhang, Yong-jun
    Dong, Yuan
    Hu, Jie-ren
    Zhang, Hui
    Han, Jing-tao
    METAL SCIENCE AND HEAT TREATMENT, 2024, 65 (9-10) : 624 - 628
  • [33] Microstructure and properties of microalloying 2205 duplex stainless steel
    Xiang H.-L.
    Chen S.-T.
    Deng L.-P.
    Zhang W.
    Zhan T.-S.
    Jilin Daxue Xuebao (Gongxueban)/Journal of Jilin University (Engineering and Technology Edition), 2020, 50 (05): : 1645 - 1652
  • [34] Hot Deformation Behavior of Duplex Stainless Steel 2205
    Zhang Yong-jun
    Dong Yuan
    Hu Jie-ren
    Zhang Hui
    Han Jing-tao
    Metal Science and Heat Treatment, 2024, 65 : 624 - 628
  • [35] Hydrogen embrittlement of SAF 2205 duplex stainless steel
    Hsu, JW
    Tsai, SY
    Shih, HC
    CORROSION, 2002, 58 (10) : 858 - 862
  • [36] Intragranularly nucleated austenite in a 2205 duplex stainless steel
    Chen, C. Y.
    Yen, H. W.
    Yu, T. H.
    Yang, J. R.
    THERMEC 2006, PTS 1-5, 2007, 539-543 : 4881 - +
  • [37] Thermal aging effect on 2205 duplex stainless steel
    WANG Zhiyu
    CHEN Xu
    BaosteelTechnicalResearch, 2017, 11 (03) : 24 - 29
  • [38] HOT DEFORMATION BEHAVIOR OF 2205 DUPLEX STAINLESS STEEL
    Chen Lei
    Wang Longmei
    Du Xiaojian
    Liu Xiao
    ACTA METALLURGICA SINICA, 2010, 46 (01) : 52 - 56
  • [39] Hydrogen behavior in SAF 2205 duplex stainless steel
    Silverstein, R.
    Sobol, O.
    Boellinghaus, Th.
    Unger, W.
    Eliezer, D.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 695 : 2689 - 2695
  • [40] Sigma phase precipitation in duplex stainless steel 2205
    Sieurin, Henrik
    Sandstrom, Rolf
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 444 (1-2): : 271 - 276