Cracking Failure Analysis of a 2205 Duplex Stainless Steel Elbow in a Natural Gas Treatment Station

被引:0
|
作者
Song, Chengli [1 ,2 ,3 ]
Song, Wenwen [4 ]
Ma, Chao [4 ]
Luo, Jinheng [1 ,2 ]
Li, Lifeng [1 ,2 ]
机构
[1] State Key Lab Oil & Gas Equipment, Xian 710077, Peoples R China
[2] CNPC Tubular Goods Res Inst, Xian 710077, Peoples R China
[3] Xian Shiyou Univ, Xian 710065, Shaanxi, Peoples R China
[4] PetroChina Tarim Oilfield Co, Koral 841000, Xinjiang, Peoples R China
关键词
Elbow; Crack; Decarbonization; Failure; DECARBURIZATION;
D O I
10.1007/s11668-024-02076-5
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A leakage accident occurred in an elbow of a natural gas processing station in western China. In order to analyze the cause of the accident, non-destructive testing, chemical composition analysis, hardness testing, metallographic examination, scanning electron microscopy analysis and other experimental analyses were carried out on the elbow. The obtained results showed that the present leakage is mainly attributed to the cracks. In fact, the microstructure around the cracks was decarburized which fully indicates that the cracks have experienced a high temperature environment. In other words, the elbow had formed initial cracks before the heat treatment process of manufacturing. Then, the cracks grew until they penetrated the wall thickness under the action of working pressure. In addition, considering that the material properties test results of the elbow meet the standard requirements, and there are no H2S, H2 and other media that cause SSC and HIC in the service environment, it is once again confirmed that the failure of the elbow is caused by defects in the original manufacturing stage. It is recommended that the same batch of elbows in service to carry out internal and external defects, and strengthen the quality inspection of the new elbows, to avoid defective elbows in the field to put into use.
引用
收藏
页码:2871 / 2878
页数:8
相关论文
共 50 条
  • [1] Welding of 2205 duplex stainless steel natural gas pipeline
    李为卫
    许晓锋
    杨扬
    刘亚旭
    胡美娟
    China Welding, 2016, 25 (03) : 49 - 56
  • [2] The characteristic of 2205 duplex stainless steel and application in natural gas pipeline
    李为卫
    赵新伟
    霍春勇
    冯耀荣
    广东有色金属学报, 2005, (Z1) : 628 - 632
  • [3] Hydrogen-enhanced cracking of 2205 duplex stainless steel
    Tsay, L. W.
    Young, M. C.
    Shin, C. -S.
    Chan, S. L. I.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (12) : 1228 - 1236
  • [4] Fatigue Cracking of Hybrid Plasma Gas Metal Arc Welded 2205 Duplex Stainless Steel
    Yurtisik, Koray
    Tirkes, Suha
    MATERIALS TESTING, 2014, 56 (10) : 800 - 805
  • [5] Hydrogen-enhanced cracking of 2205 duplex stainless steel welds
    Young, MC
    Chan, SLI
    Tsay, LW
    Shin, CS
    MATERIALS CHEMISTRY AND PHYSICS, 2005, 91 (01) : 21 - 27
  • [6] FACTORS AFFECTING THE ENVIRONMENTAL ASSISTED CRACKING BEHAVIOR OF 2205 DUPLEX STAINLESS STEEL
    Chasse, Kevin R.
    Yang, Di
    Singh, Preet M.
    Neu, Richard W.
    TMS 2010 139TH ANNUAL MEETING & EXHIBITION - SUPPLEMENTAL PROCEEDINGS, VOL 3: GENERAL PAPER SELECTIONS, 2010, : 401 - +
  • [7] Hydrogen assisted cracking of 2205 duplex stainless steel in synthetic sea water
    Michalska, J.
    Labanowski, J.
    Cwiek, J.
    TECHNOLOGIES AND PROPERTIES OF MODERN UTILISED MATERIALS (TPMUM 2012), 2012, 35
  • [8] Analysis of the failure causes in the flattening test of 2205 duplex stainless steel seamless tubes
    Qiao, Tong
    Ding, Binhua
    Dai, Weixing
    Wang, Qiming
    Cheng, Guoguang
    Zhang, Yanling
    Gao, Yuan
    ENGINEERING FAILURE ANALYSIS, 2024, 161
  • [9] Effect of heat treatment on the microstructure of duplex stainless steel 2205
    Mampuya, M. B.
    Umba, M. C.
    Mutombo, K.
    Olubambi, P. A.
    MATERIALS TODAY-PROCEEDINGS, 2021, 38 : 1107 - 1112
  • [10] Analysis for fracture toughness of 2205 duplex stainless steel pipe
    Li Wei-wei
    ENGINEERING STRUCTURAL INTEGRITY: RESEARCH, DEVELOPMENT AND APPLICATION, VOLS 1 AND 2, 2007, : 795 - 798