Hot compression deformation behavior and processing map of pure nickel N6

被引：0

作者：

School of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an ^{[1
]}

710055, China

机构：

[1] School of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an

来源：

Gongcheng Kexue Xuebao | / 4卷 / 480-487期

关键词：

Dynamic recrystallization; Hot deformation; Processing maps; Pure nickel; Rheological behavior;

D O I：

10.13374/j.issn2095-9389.2015.04.012

中图分类号：

学科分类号：

摘要：

Hot compression deformation experiment of pure nickel N6 was conducted on a Gleeble-3800 thermomechanical simulator at a deformation temperature range of 800 to 1100 ℃, a deformation rate range of 5 to 40 s-1 and at a deformation of 70%. The hot deformation behavior of this material was analyzed at high temperature and high deformation rate. The microstructural evolution and the flow stress curves were obtained at different deformation parameters. The processing maps were drawn by using the dynamic material model. Through analyzing the microstructures and the processing maps, two reasonable regions are introduced for processing pure nickel N6: the deformation temperature range of 1000 to 1100 ℃ and the deformation rate range of 5 to 7 s-1 or 20 to 40 s-1; the deformation temperature range of 800 to 900 ℃ and the deformation rate range of 5 to 10 s-1. In these two regions, the microstructure of pure nickel N6 is uniform, while in the region of rheological instability the microstructure is disordered and the grain size is varied. The grain size of pure nickel N6 after hot deformation goes up as the deformation temperature rises or the deformation rate declines. ©, 2015 All right reserved.

引用

页码：480 / 487

页数：7

共 18 条

[1] Lu Y., Zhang L.W., Deng X.H., Et al., Modeling dynamic recrystallization of pure nickel by cellular automaton, J Plast Eng, 15, 2, (2008)
[2] Zhu G.H., Xiao H.F., Sui F.L., Flow stress model of pure Al/Ni for cold deformation and its application, J Anhui Univ Technol Nat Sci, 28, 3, (2011)
[3] Huang T.L., Chen H.S., Liu Q., Et al., Effect of grain boundaries on deformation structure and microhardness in cold-rolled polycrystalline nickel, Chin J Rare Met, 31, 5, (2007)
[4] Huang T.L., Chen H.S., Liu Q., Grain orientation of large grain deformation energy storage research the influence of industrial pure nickel, The Second Session of the National Electron Back Scattering Diffraction Technology and Application of the Test Results with Electron Backscattered Diffraction (EBSD) Academic Conferences and the Sixth National Conference on Images of Materials Science and Technology, (2007)
[5] Peng H.J., Li D.F., Guo Q.M., Et al., Processing map and tube hot extrusion of GH690 alloy, Chin J Rare Met, 36, 2, (2012)
[6] Ju Q., Li D.G., Liu G.Q., The processing map of hot plastic deformation of a 15Cr-25Ni-Fe base superalloy, Acta Metall Sin, 42, 2, (2006)
[7] Cerri E., Evangelista E., McQueen H.J., Overview of the high temperature substructure development in Al-Mg alloys, High Temp Mater Processes, 18, (1999)
[8] Sellars C.M., Tegart W.J.M., On the mechanism of hot deformation, Acta Metall, 14, 9, (1996)
[9] Chen H.Q., Deng W.B., Hot Deformation behavior and microstructure evolution of TC11 titanium alloy with equiaxed structure, Chin J Rare Met, 33, 2, (2009)
[10] Feng D., Zhang X.M., Liu S.D., Et al., Constitutive equation and hot deformation behavior of homogenized Al-7.68Zn-2.12Mg-1.98Cu-0.12Zr alloy during compression at elevated temperature, Mater Sci Eng A, 608, (2014)

← 1 2 →