The Si3N4/TiN Interface: 4. Si3N4/TiN(001) Grown with a -250 V Substrate Bias and Analyzed In situ using Angle-resolved X-ray Photoelectron Spectroscopy

被引：0
作者：
Haasch, Richard T. [1 ]
Patscheider, Jörg [1 ,2 ]
Hellgren, Niklas [1 ,3 ]
Petrov, Ivan [1 ]
Greene, J.E. [1 ]
机构：
[1] University of Illinois, Department of Materials Science, Frederick Seitz Materials Research Laboratory, Urbana, IL 61801
[2] EMPA, Laboratory for Nanoscale Materials Science, CH-8600 Dübendorf
[3] Messiah College, Department of Mathematical Sciences, Grantham, PA 17027, P.O. Box 3041, One College Avenue
来源：
Surface Science Spectra | 2012年 / 19卷 / 01期
关键词：
Hard coating; Magnetron sputtering; Silicon nitride; Titanium nitride; Transition metal nitride;
D O I：
10.1116/11.20121004
中图分类号：
学科分类号：
摘要：
Angle-resolved x-ray photoelectron spectroscopy (AR-XPS) was used to analyze Si3N4/TiN(001) bilayers grown by ultrahigh vacuum reactive magnetron sputter deposition onto MgO(001), with a substrate potential of -250 V, in mixed 1:1 Ar/N2 discharges maintained at a total pressure of 0.5 Pa (3.75 × 10-3 Torr). The TiN(001) films were grown at 600 °C and the 4-ML-thick Si3N4 overlayers at room temperature. AR-XPS spectra were obtained using incident monochromatic Al Kα X-radiation at 0.83401 nm. Si3N4/TiN(001) Ti 2p spectra reveal enhanced unscreened final-state satellite peaks, compared to Ti 2p spectra obtained from uncapped TiN(001), due to decreased electronic screening induced by Si3N4/TiN(001) bilayer interfacial polarization. © 2012 American Vacuum Society.
引用
收藏
页码：62 / 71
页数：9
相关论文
共 50 条
  • [31] Microstructure evolution of the Si3N4/Si3N4 joints brazed using Au-Ni-V filler alloys with different V content
    Sun, Y.
    Zhang, J.
    Zhang, H. W.
    Fan, G. H.
    He, Y. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (33) : 8407 - 8412
  • [32] Microwave Sintering of Chessboard-Structured TiN–Si3N4 Composites Reinforced by Nanofibers
    O.B. Zgalat-Lozynskyy
    A.V. Ragulya
    Powder Metallurgy and Metal Ceramics, 2022, 61 : 32 - 39
  • [33] Preparation and properties of Si3N4 3 N 4 ceramics via vat photopolymerization using Si3N4 3 N 4 powders coated with bowl-like boehmite
    Wang, Qi-Wen
    Wu, Jia-Min
    Tian, Chong
    Shi, Zhang-Ao
    Liu, Chun-Lei
    Lin, Xin
    Xu, Hai-Sheng
    Wang, Fen
    Shi, Yu-Sheng
    ADDITIVE MANUFACTURING, 2024, 84
  • [34] Study of nanocrystalline TiN/Si3N4 thin films deposited using a dual ion beam method
    Colligon, JS
    Vishnyakov, V
    Valizadeh, R
    Donnelly, SE
    Kumashiro, S
    THIN SOLID FILMS, 2005, 485 (1-2) : 148 - 154
  • [35] Microstructure and composition of Au/Si3N4 model interface
    Suzuki, H
    Yonemitsu, K
    Saito, T
    Ikuhara, Y
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1999, 107 (12) : 1193 - 1195
  • [36] Kinetics of reaction at interface of Si3N4/W joint
    Shimoo, Toshio
    Sandjaja, Ari
    Adachi, Shin-ichiro
    Okamura, Kiyohito
    Journal of the Ceramic Society of Japan. International ed., 1995, 103 (02): : 108 - 112
  • [37] Evidence of silicide at the Ni/?-Si3N4(0001)/Si(111) interface
    Rajak, Piu
    Ciancio, Regina
    Caretta, Antonio
    Laterza, Simone
    Bhardwaj, Richa
    Jugovac, Matteo
    Malvestuto, Marco
    Moras, Paolo
    Flammini, Roberto
    APPLIED SURFACE SCIENCE, 2023, 623
  • [38] Microstructure and mechanical properties of an Si3N4/Si3N4 joint brazed with Au-Ni-Pd-V filler alloy
    Sun, Y.
    Zhang, J.
    Geng, Y. P.
    Ikeuchi, K.
    Shibayanagi, T.
    SCRIPTA MATERIALIA, 2011, 64 (05) : 414 - 417
  • [39] In situ synthesis of Fe Si particle toughening Si3N4 composite
    Sun, Xiaolin
    Sun, Kangning
    Li, Aimin
    Du, Ming
    Zhao, Yan
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2013, 37 : 142 - 147
  • [40] Si3N4–TiN Composites Produced by Hot-Pressing Silicon Nitride and Titanium Powders
    A. S. Lysenkov
    K. A. Kim
    Yu. F. Kargin
    M. G. Frolova
    D. D. Titov
    S. N. Ivicheva
    N. A. Ovsyannikov
    A. A. Konovalov
    S. N. Perevislov
    Inorganic Materials, 2020, 56 : 309 - 313
12345