Dielectric, magnetic and magnetoelectric studies on co-fired PbZr0.52Ti0.48O3-Co0.6Zn0.4Mn0.3Fe1.7O4 bilayer composite

被引：0

作者：

Gupta, Arti ^{[1
]}

Tandon, Rp ^{[1
]}

机构：

[1] Department of Physics and Astrophysics, University of Delhi, Delhi,110007, India

来源：

Materials Research Bulletin | 2015年 / 61卷

关键词：

Dielectric properties;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The maximum transverse magnetoelectric (ME) voltage coefficient αE31 ∼ 235 mV/cm Oe and maximum longitudinal ME voltage coefficient αE33 ∼ 148 mV/cm Oe were obtained in co-fired PbZr0.52Ti0.48O3-Co0.6Zn0.4Mn0.3Fe1.7O4 (PZT-CZFMO) bilayer composite (optimum thickness ratio tPZT/tCZFMO ∼ 1:3) at H = 700 Oe with an applied ac magnetic field of frequency = 1 kHz. Interestingly, at the lowest frequency of measurement f = 100 Hz, a giant value of αE31 ∼ 16.9 V/cm Oe was observed for this bilayer system that is orders of magnitude higher than the reported αE values (∼200-300 mV/cm Oe) for PZT-CFO composite structures at low frequencies. Better magneto-mechanical coupling resulting from the simultaneous substitution of both Mn and Zn in CFO along with the optimum thickness ratio of two layers must be the cause of substantial ME coupling in the PZT-CZFMO bilayer system. In addition, the dielectric constant spectra of bilayer revealed very high thickness resonance frequency ∼85 MHz and band width ∼14 MHz. © 2014 Elsevier Ltd.

引用

页码：231 / 237