Erosion behavior of various high chromium cast iron alloys exposed to gas-blast stream of ferric oxide particles

被引：0

作者：

Kalantarian, R. ^{[1
,2
]}

Kiayee, N. ^{[1
]}

Farzadi, A. ^{[1
]}

Omidvar, H. ^{[1
]}

机构：

[1] Amirkabir Univ Technol, Dept Mat & Met Engn, Tehran 15916, Iran

[2] Khuzestan Steel Co KSC, Ahvaz, Iran

来源：

ENGINEERING FAILURE ANALYSIS | 2024年 / 163卷

关键词：

Hardfacing; Flux-cored arc welding; Gas blasting erosion test; Microstructure; Primary carbide; Solid particle erosion; WEAR PROPERTIES; MICROSTRUCTURE; HARDNESS; RESISTANCE; CARBIDE; NIOBIUM; STEEL; MO;

D O I：

10.1016/j.engfailanal.2024.108520

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Depositing hardfacing material onto a surface with the welding method is a common way of protecting surfaces against wear damage. In this study, five high chromium hardfacing alloys were used to prepare samples for the gas blasting erosion test. Erodent particles were ferric oxide specks with a hardness of 657 HV and an average size of 260 mu m. Impinging stream eroded the surface of samples with the gas flow of 100 m/s at an angle of 30 degrees while the particle feed was increased from 140 to 630 g. The results indicated that erosion resistance is dominated by bulk hardness of hardfaced alloys. In addition, the erosion rate for a sample containing Mo, Nb, V, and W was the lowest since it had the highest bulk hardness among all other samples.

引用

页数：14

共 39 条

[21] Growth characteristics of primary M7C3 carbide in hypereutectic Fe-Cr-C alloy [J].

Liu, Sha ;

Zhou, Yefei ;

Xing, Xiaolei ;

Wang, Jibo ;

Ren, Xuejun ;

Yang, Qingxiang .

SCIENTIFIC REPORTS, 2016, 6

[22]

Ma YP, 2012, CHINA FOUNDRY, V9, P148

[23]

Raynor G.V., 1988, Phase Equilibrium in Iron Ternary Alloys, VFirst

[24] Erosive wear behaviour of weld hardfacing high chromium cast irons: effect of erodent particles [J].

Sapate, SG ;

RamaRao, AV .

TRIBOLOGY INTERNATIONAL, 2006, 39 (03) :206-212

[25] Influence of niobium on the microstructure and wear resistance of iron-based hardfacings produced by pre-placement technique-a novel approach [J].

Singla, Yogesh Kumar ;

Arora, Navneet ;

Dwivedi, D. K. ;

Rohilla, Vinod .

INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2017, 93 (5-8) :2667-2674

[26] Variations in microstructure of high chromium cast irons and resultant changes in resistance to wear, corrosion and corrosive wear [J].

Tang, X. H. ;

Chung, R. ;

Li, D. Y. ;

Hinckley, B. ;

Dolman, K. .

WEAR, 2009, 267 (1-4) :116-121

[27] Effect of Ni on microstructure and wear behaviour of 13Cr-W-Mo-2C white cast iron [J].

Teker, Tanju ;

Yilmaz, S. Osman .

REVISTA DE METALURGIA, 2023, 59 (02)

[28] Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements [J].

Touhami, Rim Chaima ;

Mechachti, Said ;

Bouhamla, Khedidja ;

Hadji, Ali ;

Khettache, Abdelkader .

METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS, 2023, 12 (04) :580-590

[29] Effect of the simultaneous Ti and W addition on the microstructure and wear behavior of a high chromium white cast iron [J].

Vapeani Guerra, Francisco ;

Bedolla-Jacuinde, Arnoldo ;

Zuno-Silva, Jorge ;

Mejia, Ignacio ;

Cardoso-Legorreta, Edgar ;

Arenas-Flores, Alberto .

METALLURGICAL RESEARCH & TECHNOLOGY, 2019, 116 (06)

[30] Microstructure and Erosion Wear Characterization of a New Cast High-Vanadium-Chromium Alloy (HVCA) [J].

Wang, Fangfang ;

Xu, Liujie .

INTERNATIONAL JOURNAL OF METALCASTING, 2023, 17 (01) :466-480

← 1 2 3 4 →