Flexural performance of ultra-high performance fiber reinforced cementitious composite material doped with copolymer formaldehyde fiber

被引：0
|
作者：
Wang C. [1 ]
Zhang Y. [1 ]
Duan L. [1 ]
机构：
[1] School of Highway, Chang'an University, Xi'an
来源：
Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2024年 / 41卷 / 01期
关键词：
copolymer formaldehyde fiber; fiber content; fiber type; flexural performance; ultra-high performance fiber reinforced cementitious composite material;
D O I：
10.13801/j.cnki.fhclxb.20230524.003
中图分类号：
学科分类号：
摘要：
In order to investigate the flexural performance of ultra-high performance fiber reinforced cementitious composite material (UHPFRC) doped with copolymer formaldehyde fiber, five groups of bending specimens were designed and tested, including three groups of single mixed specimens and two groups of fiber hybrid specimens. The results show that among the copolymer formaldehyde fiber UHPFRC specimens, 2vol% copolymer formaldehyde fiber UHPFRC specimens have better flexural strength, with an average strength of 13.4 MPa. An appropriate amount of co-formaldehyde fiber can delay the cracking of UHPFRC matrix and enhance its ability to deformation before cracking. Among the five groups of test pieces, the cracking deflection of 2vol% copolymer formaldehyde fiber UHPFRC test piece is the largest, which can reach 0.65 mm. Hybrid fiber can better enhance the flexural strength and toughness of UHPFRC. When 1.5vol% copolymer formaldehyde fiber and 1.5vol% steel fiber are mixed, the flexural strength of UHPFRC specimens can reach 13.9 MPa, and the toughness of this group of specimens is the best. The research reveals the effect of copolymer formaldehyde fiber on the flexural mechanical properties of UHPFRC, which has important reference value for its application in UHPFRC and the promotion of UHPFRC. © 2024 Beijing University of Aeronautics and Astronautics (BUAA). All rights reserved.
引用
收藏
页码：373 / 382
页数：9
相关论文
共 27 条
  • [1] CHEN Baochun, JI Tao, HUANG Qingwei, Et al., Review of research on ultra-high performance concrete, Journal of Architecture and Civil Engineering, 31, 3, pp. 1-24, (2014)
  • [2] CHEN Baochun, LIN Yijun, YANG Jian, Et al., Review on fiber function in ultra-high performance fiber reinforced concrete, Journal of Fuzhou University (Natural Science Edition), 48, 1, pp. 58-68, (2020)
  • [3] ZHAO Renda, ZHAO Chenggong, YUAN Yuan, Et al., Research progress on application of steel fiber in UHPC[J], China Journal of Highway and Transport, 34, 8, pp. 1-22, (2021)
  • [4] WANG Yichao, HOU Mengjun, YU Jiangtao, Et al., Experimental study on mechanical properties of ultra-high ductile cementitious composites[J], Materials Reports, 32, 20, pp. 3535-3540, (2018)
  • [5] HUANG Zhengyu, LI Caowang, LIU Yongqiang, The effects of polyethylene fiber on the properties of UHPC, Materials Reports, 28, 20, pp. 111-115, (2014)
  • [6] LAI Jianzhong, XU Sheng, YANG Chunmei, Et al., Influence of polyvinyl alcohol fibers on the properties of ultra high performance concrete at high temperature, Journal of Nanjing University of Science and Technology, 37, 4, pp. 633-639, (2013)
  • [7] CHEN Qian, XU Lihua, WU Fanghong, Et al., Experimental investigation on strength of steel-polypropylene hybrid fiber reinforced ultra high performance concrete, Bulletin of the Chinese Ceramic Society, 39, 3, pp. 740-748, (2020)
  • [8] TENG Xiaodan, TAN Youwen, LI Pengyuan, Et al., Mechanical properties of steel-UHMWPE fiber reinforced concrete after high temperature, Bulletin of the Chinese Ceramic Society, 38, 4, pp. 996-1001, (2019)
  • [9] YAN Luhui, ZHANG Yuwu, ZHU Lin, Basic mechanical properties of ultra high molecular weight polyethylene fiber concrete[J], Journal of National University of Defense Technology, 36, 6, pp. 43-47, (2014)
  • [10] AN Yukun, WANG Yatao, LI Jianhua, Study on shrinkage and permeability of polyoxymethylene fiber reinforced concrete, Concrete World, 3, pp. 64-67, (2019)
123