Preparation and properties of blocked solvent-free polyurethane ultrafine synthetic leather base cloth

被引：0
|
作者：
He Y. [1 ]
Ma X. [1 ]
Ding B. [1 ]
Wu X. [1 ]
He Y. [1 ]
Zheng S. [1 ]
机构：
[1] College of Bioresources Chemical and Materials Engineering, Shaanxi University of Science & Technology, Xi'an
来源：
He, Yuanxin (dandelion2007@hotmail.com) | 1600年 / Beijing University of Aeronautics and Astronautics (BUAA)卷 / 38期
关键词：
Blocked solvent-free polyurethane; Composite materials; Mechanical property; Microstructure; Synthetic leather;
D O I：
10.13801/j.cnki.fhclxb.20200601.001
中图分类号：
学科分类号：
摘要：
Blocked solvent-free polyurethane (BSFPU) ultrafine synthetic leather base cloth was composed of polyamide 6-alkali soluble polyester (PA6-COPET) sea-island fiber nonwoven and blocked solvent-free polyurethane through impregnation, alkali decrement and finishing method. Microstructures changing during preparation were observed by scanning electron microscope, and then the effect of BSFPU leaching ratio on the mechanical property and hygienic performance of BSFPU ultrafine synthetic leather base cloth was studied. The results show that the sea island fibers are reduced to 37 bundles with a diameter of about 3 μm and the microstructure similar to natural leather is observed in BSFPU ultrafine synthetic leather base cloth. With the BSFPU leaching ratio increasing, the deweighting rate in the process of alkali decrement goes down from 31.59wt% to 28.22wt%; the elongation at break and tear strength of BSFPU ultrafine synthetic leather base cloth reduce continuously; the tensile strength almost remains the same result and the number begins to decline until the leaching ratio above 100wt%; the air permeability also decreases from 50 086 mL/(m2·s) to 24 757 mL/(m2·s) and the water vapor permeability reduces from 790.47 mg/(10 cm2·24 h) to 488.70 mg/(10 cm2·24 h). After testing, BSFPU ultrafine synthetic leather base cloth can meet the industry standards and its hygienic performance is significantly higher than commercially available solvent-based polyurethane ultrafine synthetic leather base cloth. Copyright ©2021 Acta Materiae Compositae Sinica. All rights reserved.
引用
收藏
页码：389 / 397
页数：8
相关论文
共 26 条
  • [1] CHEN M, ZHOU D L, CHEN Y, Et al., Analyses of structures for a synthetic leather made of polyurethane and microfiber, Journal of Applied Polymer Science, 103, 2, pp. 903-908, (2007)
  • [2] WANG X C, XU N, GUO P Y, Et al., Improving moisture absorbent and transfer abilities by modifying superfine fiber synthetic leather base with collagen-chrome tannins, Textile Research Journal, 86, 7, pp. 765-775, (2016)
  • [3] XU X, WU Z P., Environmental cost analysis and upgrading research of synthetic leather industry, Enrgy Procedia, 5, pp. 1341-1347, (2011)
  • [4] DUO Y C, QIAN X M, ZHAO B B, Et al., Improving hygiene performance of microfiber synthetic leather base by mixing polyhydroxybutyrate nanofiber, Journal of Engineered Fibers and Fabrics, 14, pp. 1-7, (2019)
  • [5] SUR S H, CHOI P J, KO J W, Et al., Preparation and properties of DMF-based polyurethanes containing bio-polyol/ester-polyol for wet-type polyurethane artificial leather, Clean Technology, 25, 1, pp. 7-13, (2019)
  • [6] JIANG Zhiqing, YIN Dehe, CHEN Jianmin, Et al., Production of figured sea-island fiber and its application in microfiber leather, Advance Textile Technology, 26, 3, pp. 29-33, (2018)
  • [7] FENG Jianyan, WANG Xuechuan, ZHANG Zhe, Et al., Analysis and discussion on the development trend of green clean production of polyurethane synthetic leather, Leather Science and Engineering, 28, 1, pp. 25-29, (2018)
  • [8] ZHAO Baobao, QIAN Yao, LIU Fan, Et al., Preparation and properties of hollow segment-pie microfiber/waterborne polyurethane synthetic leather, Acta Materiae Compo-site Sinica, 34, 11, pp. 2392-2400, (2017)
  • [9] LIU Ruowang, CHEN Yi, XU Gang, Et al., Application of acrylate emulsion in manufacture of waterborne microfiber synthetic leather base, China Leather, 46, 6, pp. 52-58, (2017)
  • [10] LUO Xiaomin, WEI Mengyuan, FENG Jianyan, Et al., Preparation of waterborne polyurethane with high solid content and its application in superfine fiber synthetic leather, Paint &Coating Industry, 48, 2, pp. 64-68, (2018)
123