Room temperature gas sensors for NH3 detection based on the heterojunction of 2D Ti3C2Tx MXenes and Bi2S3

Bi2S3/Ti3C2Tx nanomaterials were successfully prepared through a simple hydrothermal method. Various methods were used for their characterization, including XRD, XPS, SEM, EDS, and BET, along with testing their gas-sensing properties. The results showed that the response value to 100 ppm ammonia at room temperature reached 107%, which was 14.1 times higher than that of pure few-layer MXene. After undergoing anti-humidity interference testing, we observed that Bi2S3/Ti3C2Tx exhibited a higher response value in real-time monitoring of ammonia as humidity increased. Specifically, under 90% humidity conditions, its response value reached 1.32 times that of normal humidity conditions. This exceptional moisture resistance ensures that the sensor can maintain stability, and even exhibit superior performance, in harsh environments. Therefore, it possesses excellent selectivity, high-moisture-resistance, and long-term stability, making it significant in the field of medical and health monitoring.