Melamine formaldehyde resin adhesive toughened with graphene oxide: Structures and properties

被引：0
|
作者：
Xu, Xiaoxue [1 ]
Zhang, Bengang [2 ]
Yu, Liping [1 ]
Li, De [1 ]
Wu, Zhigang [1 ]
Liang, Jiankun [3 ]
Lei, Hong [4 ]
机构：
[1] College of Forestry, Guizhou University, Guiyang,550025, China
[2] Jiangxi Academy of Forestry, Nanchang,330032, China
[3] College of Civil Engineering, Kaili University, Qiandongnan, 556011, China
[4] School of Chemistry and Material Engineering, Zhejiang A&F University, Hangzhou,311300, China
来源：
Polymer Testing | 2024年 / 138卷
关键词：
All Open Access; Gold;
D O I：
10.1016/j.polymertesting.2024.108557
中图分类号：
学科分类号：
摘要：
Curing
引用
收藏
相关论文
共 50 条
  • [41] Synthesis of melamine-glucose resin adhesive
    CHEN Shuanhu & ZHANG Lei Department of Chemistry
    Science China Chemistry, 2005, (S1) : 29 - 32
  • [42] Synthesis of melamine-glucose resin adhesive
    Shuanhu Chen
    Lei Zhang
    Science in China Series B: Chemistry, 2005, 48 : 29 - 32
  • [43] Synthesis of melamine-glucose resin adhesive
    Chen, SH
    Zhang, L
    SCIENCE IN CHINA SERIES B-CHEMISTRY, 2005, 48 (Suppl 1): : 29 - 32
  • [44] Effect of Melamine Allocation Proportion on Chemical Structures and Properties of Melamine-Urea-Formaldehyde Resins
    Luo, Jianlin
    Zhang, Jizhi
    Luo, Jing
    Li, Jianzhang
    Gao, Qiang
    BIORESOURCES, 2015, 10 (02): : 3265 - 3276
  • [45] Structures and Properties of Benzoguanamine Modified Melamine Formaldehyde/Polyvinyl Alcohol Fibers
    Zhou Y.
    Yu J.
    Shen Y.
    Wang Y.
    Zhu J.
    Hu Z.
    Yu, Junrong (yjr@dhu.edu.cn), 1600, Sichuan University (33): : 50 - 55
  • [46] Influence of the melamine content in melamine-urea-formaldehyde resins on formaldehyde emission and cured resin structure
    Tohmura, S
    Inoue, A
    Sahari, SH
    JOURNAL OF WOOD SCIENCE, 2001, 47 (06) : 451 - 457
  • [47] Influence of the melamine content in melamine-urea-formaldehyde resins on formaldehyde emission and cured resin structure
    Shin-ichiro Tohmura
    Akio Inoue
    Siti Hanim Sahari
    Journal of Wood Science, 2001, 47 : 451 - 457
  • [48] Phenol-formaldehyde resin enriched with graphene nanoplatelets as an electroconductive adhesive for wood composites
    Lukawski, Damian
    Hochmanska-Kaniewska, Patrycja
    Baleczny, Wojciech
    Martin, Anna
    Janiszewska-Latterini, Dominika
    Lekawa-Raus, Agnieszka
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 132
  • [49] Mechanical and thermal properties of biphenyldiol formaldehyde resin/gallic acid epoxy composites enhanced by graphene oxide
    Chen, Shihui
    Lv, Shufang
    Hou, Guixiang
    Huo, Li
    Gao, Jungang
    JOURNAL OF APPLIED POLYMER SCIENCE, 2015, 132 (41)
  • [50] Utilization of carbon black from Mao bamboo as reinforcing agent for melamine urea formaldehyde resin wood adhesive
    Liu, Jinming
    Mo, Hailin
    Xie, Enjun
    Fang, Jianlin
    Hou, Zhibing
    Gan, Weixing
    Industrial Crops and Products, 2022, 187
12345