Effect of Corrosion Products of Crack Face by Nitric Acid on Fatigue Crack Propagation Properties

被引：0
作者：
Shibata H. [1 ]
Luo P. [2 ]
Satoh K. [1 ]
Yonezawa T. [3 ]
Tsutsumi S. [2 ]
机构：
[1] Sumitomo Heavy Industries, Ltd., Natsushima-cho, Yokosuka
[2] Nippon Steel Corporation, Futtsu, Shintomi
[3] Osaka University, Yamadaoka, Suita
来源：
Zairyo/Journal of the Society of Materials Science, Japan | 2023年 / 72卷 / 12期
关键词：
Corrosion products; Crack closure; Fatigue life extension; Structural steel; Wedge effect;
D O I：
10.2472/JSMS.72.873
中图分类号：
学科分类号：
摘要：
Recently, multiple fatigue life extension techniques have been proposed utilizing crack closure, while no detailed mechanisms have been discussed for them. On the other hand, the authors have proposed the assessment method on crack initiation and propagation life based on an elasto-plastic model, and that would work for better assessment with detailed mechanisms of them. In this paper, fatigue crack growth tests were carried out using SENT specimens corroded at the crack length of 3mm by 35% HNO3, and shape measurements for fractured specimens were conducted after the tests. The results show that crack growth rates are retarded due to corrosion products between crack faces (Wedge effect). Furthermore, corrosion products distribute on the crack faces with 20 to 50µm thickness, which suggests correlations between the thickness of corrosion products and the level of life extension effect. ©2023 The Society of Materials Science, Japan.
引用
收藏
页码：873 / 878
页数：5
相关论文
共 12 条
  • [1] Hirou sekkei binran, (1995)
  • [2] Elber W., Fatigue crack closure under cyclic tension, Engineering Fracture Mechanics, 2, 1, pp. 37-45, (1970)
  • [3] Takahashi I., Takahashi C., Kotani N., Restraint of fatigue crack propagation by wedge effect of fine particles, Journal of the Society of Naval Architects of Japan, 1998, 184, pp. 361-367, (1998)
  • [4] Takahashi I., Ushijima M., Takahashi C., Uematsu S., Kotani N., Automatic restraint and visual detection of fatigue crack growth by applying an alumina paste, Quarterly Journal of the Japan Welding Society, 22, 4, pp. 531-541, (2004)
  • [5] Takahashi I., Hirokiretsu no shinntenn yokusei/kensyutsu houhou, oyobi hirokiretsu no shinntenn yokusei/kensyutsu shi-to, (2021)
  • [6] Putri C. A., Tateishi K., Shimizu M., Hanji Y., Retardation of fatigue crack growth by corrosion accelerator injection, Steel Construction Engineering, 28, 112, pp. 111-116, (2021)
  • [7] Tsutsumi S., Fincato R., Cyclic plasticity model for fatigue with softening behavior below macroscopic yielding, Materials & Design, 165, pp. 1-16, (2019)
  • [8] Tsutsumi S., Nagahama H., Kiyokawa Y., Fincato R., Fatigue crack propagation life assessment of steel predicted by local elastoplasticity response – surface crack propagation property in steel concentration field, Journal of Japan Society of Civil Engineers, Ser. A2, 76, 2, pp. I399-I410, (2020)
  • [9] Morita K., Mouri M., Ayang B., Fincato R., Tsutsumi S., Evaluation of fatigue crack propagation behavior in low carbon steel and their simulated HAZ and fatigue life assessment of non-load carrying welded fillet joint. (Assessment of fatigue performance of welded joints considering cyclic elasto-plasticity response.), Quarterly Journal of the Japan Welding Society, 40, 1, pp. 27-35, (2022)
  • [10] Yonezawa T., Li B., Tsutsumi S., Evaluation of fatigue crack initiation and propagation life of structural steel based on local strain measurement by DIC, Tetsu-to-Hagané, 108, 10, pp. 762-771, (2022)
12