Mechanical behavior of half-grouted sleeve connection under the coupling of sulfate erosion and dry-wet cycles

被引：0
|
作者：
Wang, Tongxing [1 ]
Wen, Jianian [1 ]
Hu, Menghan [2 ]
Han, Qiang [1 ]
机构：
[1] Beijing Univ Technol, State Key Lab Bridge Safety & Resilience, Beijing 100124, Peoples R China
[2] Beijing Univ Civil Engn & Architecture, Sch Civil & Transportat Engn, Beijing 100044, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2024年 / 456卷
基金：
中国国家自然科学基金;
关键词：
Precast structure; Half-grouted sleeve; Sulfate erosion; Dry-wet cycle; Bond-slip; REINFORCED-CONCRETE; WETTING CYCLES; SPLICE SLEEVE; BOND BEHAVIOR; ATTACK; SLIP; ANCHORAGE;
D O I：
10.1016/j.conbuildmat.2024.139281
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
The half-grouted sleeve connection (HGSC) is commonly used in precast concrete (PC) structures due to its convenient fabrication method, however, the long-term mechanical properties of the HGSC in corrosive environments remain unclear. Therefore, the mechanical behavior of HGSC under the coupling of sulfate erosion and dry-wet cycles (DWCs) is investigated in this paper. A total of 24 specimens with 4d and 8d embedded lengths were designed and subjected to sulfate erosion with different DWCs. The failure modes and mechanical properties of HGSCs with different embedded lengths and DWCs were comparatively analyzed. Following this, a modified bond-slip model considering sulfate erosion was proposed and validated against the measured data. The test results indicated that the failure modes of HGSCs with 4d and 8d embedded lengths were rebar fracture and slip failure, respectively. As the number of sulfate erosions increased, the performance indicators of HGSCs gradually decreased. After 180 dry-wet cycles (DWCs), the average deformation and average slip under peak load for HGSCs with an embedded length of 8d decreased by 36.6 % and 37.7 %, respectively. In contrast, for HGSCs with an embedded length of 4d, the corresponding values increased by 3.0 % and 40.1 %, respectively. The predicted bond-slip model of HGSC considering sulfate erosion agreed well with the experimental results, and it can be useful in the life-cycle modeling of the PC structures with HGSCs.
引用
收藏
页数：18
相关论文
共 32 条
  • [1] Study on the mechanical properties of desert sand concrete under dry-wet cycles with sulfate erosion
    Xu, Wenjing
    Liu, Haifeng
    Qin, Dongyang
    Doh, Shu Ing
    PHYSICS AND CHEMISTRY OF THE EARTH, 2025, 138
  • [2] Erosion damage and expansion evolution of interfacial transition zone in concrete under dry-wet cycles and sulfate erosion
    Zheng, Suining
    Qi, Lin
    He, Rui
    Wu, Jiangtao
    Wang, Zhenjun
    CONSTRUCTION AND BUILDING MATERIALS, 2021, 307
  • [3] Experimental investigation on the connection performance of defect detectable and repairable half-grouted sleeve under cyclic loads
    Xie, Linlin
    Zhong, Bojian
    Chen, Xi
    Miao, Qisong
    Liu, Qianmin
    Yang, Cantian
    Wang, Xinyu
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 323
  • [4] Experimental study and numerical simulation on tensile behavior of eccentric rebar connection for half-grouted sleeve splice
    Chen J.
    Wang Z.
    Ju S.
    Liu Z.
    Jianzhu Jiegou Xuebao/Journal of Building Structures, 2020, 41 : 160 - 171
  • [5] Damage mechanism and interfacial transition zone characteristics of concrete under sulfate erosion and Dry-Wet cycles
    He, Rui
    Zheng, Suining
    Gan, Vincent J. L.
    Wang, Zhendi
    Fang, Jianhong
    Shao, Yu
    CONSTRUCTION AND BUILDING MATERIALS, 2020, 255
  • [6] Durability Analysis of Industrial Waste Stabilized Sludge Subjected to Dry-Wet Cycles and Sulfate Erosion
    Shi, Fangzhen
    Wang, Qiang
    Wu, Liuyan
    Yang, Chenglong
    Yang, Liu
    ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2025, 50 (03) : 1615 - 1631
  • [7] Mechanical Properties and Microstructure of Rubber Concrete under Coupling Action of Sulfate Attack and Dry-Wet Cycle
    Wang, Heng
    Pang, Jianyong
    SUSTAINABILITY, 2023, 15 (12)
  • [8] Sulfate Durability of Aeolian Sand Concrete Under Dry-Wet Cycles and Sand Blowing
    Dong R.
    Shen X.
    Xue H.
    Liu Q.
    Wei L.
    Cailiao Daobao/Materials Reports, 2020, 34 (20): : 20053 - 20060
  • [9] Chloride diffusion behavior of engineered cementitious composite under dry-wet cycles
    Sun, Renjuan
    Hu, Xinlei
    Ling, Yifeng
    Zuo, Zhiwu
    Zhuang, Peizhi
    Wang, Fei
    CONSTRUCTION AND BUILDING MATERIALS, 2020, 260
  • [10] Effect of Bermuda grass root on mechanical properties of soil under dry-wet cycles
    Ma, Qiang
    Wu, Nianze
    Xiao, Henglin
    Li, Zhi
    Li, Wentao
    BULLETIN OF ENGINEERING GEOLOGY AND THE ENVIRONMENT, 2021, 80 (09) : 7083 - 7097
1234