Damage Characteristics and Crack Monitoring of Corroded Reinforced Concrete Beams in Bending Process Based on Acoustic Emission Techniques

被引：0
|
作者：
Pan T. [1 ]
Zheng Y. [1 ]
Xu X. [1 ]
Lan X. [1 ]
Zhou Y. [2 ]
机构：
[1] School of Civil Engineering, Tongji University, Shanghai
[2] College of Architecture and Engineering, Sanming College, Sanming
来源：
Tongji Daxue Xuebao/Journal of Tongji University | 2024年 / 52卷 / 03期
关键词：
acoustic emission; b value; concrete cracking; flexural characteristics; steel corrosion;
D O I：
10.11908/j.issn.0253-374x.23110
中图分类号：
学科分类号：
摘要：
Reinforcement corrosion has been one of the major causes of degradation of reinforced concrete structures. Identifying the internal damage signals of corroded RC structures will provide a theoretical basis for structural health monitoring of existing buildings. This study investigated the effect of steel corrosion on the flexural characteristics of RC beams at the microscopic crack level using acoustic emission（AE）technique. The rise time/peak amplitude （R/A），ringing count/duration （AF）and improved b（Ib）values of the acoustic emission signal were calculated for reflecting the changes in cracking patterns and damage modes of corroded RC beams. The results show that the ultimate load capacity of rusted reinforced concrete beams decreases significantly with the increase of reinforcement corrosion rate. there is a good correspondence between acoustic emission signal and concrete damage，and the damage process of the specimen can be divided into three damage stages：initial damage stage，damage evolution stage，and sustained damage growth stage. Besides，the trend of b-value curve can reflect the formation and development of cracks. Moreover，with the increase of load，the proportion of shear cracks in the specimen gradually increases，and the higher the degree of corrosion of the specimen in the sustained damage stage，the higher the proportion of shear cracks. © 2024 Science Press. All rights reserved.
引用
收藏
页码：350 / 359
页数：9
相关论文
共 24 条
  • [1] SUN Junzu, HUANG Qiao, REN Yuan, Mechanical properties test of steel reinforcement in concrete after corrosion fatigue［J］, Journal of Harbin Institute of Technology, 48, 3, (2016)
  • [2] MOHAMMED T A., Service life prediction of reinforced concrete structures subjected to corrosion：a comparative study［J］, International Journal of Structural Integrity, 14, 3, (2023)
  • [3] HWANG W，ANN KY., Determination of rust formation to cracking at the steel-concrete interface by corrosion of steel in concrete ［J］, Construction and Building Materials, 367, (2023)
  • [4] AHMAD S., Reinforcement corrosion in concrete structures，its monitoring and service life prediction―a review［J］, Cement Concrete Composites, 25, 4, (2003)
  • [5] NOORSIHADA M N., An overview on fatigue damage assessment of reinforced concrete structures with the aid of acoustic emission technique［J］, Construction and Building Materials, 112, (2016)
  • [6] MIRGAL P，, BANERJEE S，, Et al., Application of Acoustic Emission as Damage Assessment Technique for Performance Evaluation of Concrete Structures：A Review［J］, Practice Periodical on Structural Design and Construction, 28, 3, (2023)
  • [7] ZHOU Y B，, Et al., Damage pattern recognition for corroded beams strengthened by CFRP anchorage system based on acoustic emission techniques［J］, Construction and Building Materials, 406, (2023)
  • [8] Acoustic emission monitoring and damage assessment of FRP-strengthened reinforced concrete columns under cyclic loading［J］, Construction and Building Materials, 144, (2017)
  • [9] LIU SM, Et al., Fracturing mechanism of coal-like rock specimens under the effect of non-explosive expansion［J］, International Journal of Rock Mechanics And Mining Sciences, 103, (2018)
  • [10] Dan WU, JIN Xianyu, FU Chuanqing, Et al., Study on acoustic emission b-value of load damage in corroded reinforced concrete columns［J］, Concrete, 12, (2016)
123