Influence of CoFe2O4 content on the multifunctional properties of BiFeO3-CoFe2O4 core-shell nanocomposites

The utilization of magnetoelectric composites, particularly core-shell configurations, enhances their versatile applications in various sectors such as medicine and data storage. Among these composites, the perovskite-spinel combination is distinguished by its significant potential. A series of (1-x) BiFeO3-(x) CoFe2O4 (where x = 0.0, 0.2, 0.5, and 1.0) nano core-shell structures were synthesized using a sol-gel auto-combustion method to explore their multifunctional capabilities. Structural analyses identified peaks corresponding to both perovskite and spinel phases. Field Emission Scanning Electron Microscopy revealed a reduction in average particle size with an increase in CoFe2O4 content.The particle size in the BFO80-CFO20 sample has been reduced from 243 nm to 34 nm. Additionally, Transmission Electron Microscopy images of the BFO80-CFO20 sample highlighted the evolution of core-shell structures. Our findings indicate that higher CFO concentrations significantly affect the dielectric, ferroelectric, and optical properties. The bandgaps of the nanocomposites BFO80-CFO20 and BFO50CFO50 were estimated to be 1.43 eV and 1.39 eV, respectively. Magnetic analysis showed increases in both saturation magnetization and remanent magnetization with increased CFO content, while the coercive field followed a different trend. The saturation magnetization values for the samples BFO, BFO80-CFO20, BFO50CFO50, and CFO were calculated as 0.205, 14.612, 28.374, and 74.105 emu , respectively. The measured values for the same samples were 0.08, 5.07, 11.34, and 34.01 emu , respectively. Further, the electrochemical properties were thoroughly investigated using cyclic voltammetry, linear sweep voltammetry, and electrochemical impedance spectroscopy.