The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water

被引：0
|
作者：
Bian, W. W. [1 ]
Lu, Y. H. [1 ]
Kang, L. Z. [1 ]
Zhang, X. F. [1 ]
Xin, L. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, 6-6-10 Aramaki Aoba,Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 690; TT; Impact fretting corrosion; Oxidation; Microstructure; SURFACE OXIDE-FILMS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; NANOLAMINATED STRUCTURE; ALLOY; 690TT; DEFORMATION; TUBES; SUPERALLOY; EVOLUTION; DIFFUSION;
D O I：
10.1016/j.corsci.2024.112507
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The impact fretting corrosion of Inconel 690TT under different impact forces was investigated. The results indicated that there was a competitive relationship between formation of third body layer (TBL) and fragmentation of TBL caused by impact force. With the increase of impact forces, damage mechanism changed from adhesive wear to delamination wear, and crack initiation sites gradually shifted from TBL to internal oxidation zone in tribologically transformed structure (TTS) layer. Nanocrystalline boundaries and defects induced by impact force provided channels for internal oxidation. The formation mechanism of TTS was the combined effect of continuous dynamic recrystallization (cDRX) and twin-assisted cDRX.
引用
收藏
页数：19
相关论文
共 45 条
  • [31] Impact fretting wear of Inconel 690 tube with different supporting structure under cycling low kinetic energy
    Sun, Yang
    Cai, Zhen-bing
    Chen, Zhi-qiang
    Qian, Hao
    Tang, Li-chen
    Xie, Yongcheng
    Zhou, Zhong-rong
    Zhu, Min-hao
    WEAR, 2017, 376 : 625 - 633
  • [32] Electrochemical Corrosion Performance of Mechanically Polished Alloy 690TT at High-Temperature Water (200°C)
    Arjmand, Farzin
    Zhang, Lefu
    CORROSION, 2015, 71 (12) : 1481 - 1489
  • [33] Study on the SCC behavior induced by creep cavities on scratched surface of Alloy 690TT in high temperature water
    Wang, X. Y.
    Shang, C. G.
    Li, Z. H.
    Bai, Y. K.
    Liu, T. G.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2022, 196
  • [34] Impact of dissolved oxygen concentration on the coupling damage between fretting wear and corrosion on zirconium alloy cladding tube in high temperature pressurized water
    Wang, Shuji
    Zhang, Yusheng
    Ming, Hongliang
    Wang, Jiazhen
    Wang, Jianqiu
    Han, En-Hou
    WEAR, 2025, 572
  • [35] Fretting corrosion running regime and damage mechanism evolution of zirconium alloy mated with Inconel 718 alloy in high temperature high pressure water environment
    Kang, L. Z.
    Lu, Y. H.
    Bian, W. W.
    Xin, L.
    Han, Y. M.
    TRIBOLOGY INTERNATIONAL, 2024, 194
  • [36] Corrosion Fatigue Crack Growth Behavior of Alloy 690 in High-Temperature Pressurized Water
    Chen, Kai
    Du, Donghai
    Zhang, Lefu
    Andresen, Peter L.
    CORROSION, 2017, 73 (06) : 724 - 733
  • [37] Fretting wear between Alloy 690 and 405 stainless steel in high temperature pressurized water with different normal force and displacement
    Ming, Hongliang
    Liu, Xingchen
    Lai, Jiang
    Wang, Jianqiu
    Gao, Lixia
    Han, En-Hou
    JOURNAL OF NUCLEAR MATERIALS, 2020, 529
  • [38] CORROSION BEHAVIOR OF NUCLEAR GRADE ALLOYS 690 AND 800 IN SIMULATED HIGH TEMPERATURE AND HIGH PRESSURE PRIMARY WATER OF PRESSURIZED WATER REACTOR
    Li Xiaohui
    Wang Jianqiu
    Han En-Hou
    Ke Wei
    ACTA METALLURGICA SINICA, 2012, 48 (08) : 941 - 950
  • [39] The role of normal force on the fretting corrosion behaviour of alloy 690 TT tube against 410 stainless steel plate in high temperature high pressure water
    Wang, Shicheng
    Deng, Xiaoyun
    You, Lei
    Hu, Kangkai
    Ren, Lu
    Gao, Wei
    Xu, Jian
    Yu, Hongying
    Sun, Dongbai
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 6162 - 6181
  • [40] Fretting corrosion behavior and microstructure evolution of hydrided zirconium alloy under gross slip regime in high temperature high pressure water environment
    Kang, L. Z.
    Lu, Y. H.
    Bian, W. W.
    Yu, P. J.
    Wang, Y. . B.
    Xin, L.
    Han, Y. M.
    CORROSION SCIENCE, 2025, 242
12345