The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water

被引：0
|
作者：
Bian, W. W. [1 ]
Lu, Y. H. [1 ]
Kang, L. Z. [1 ]
Zhang, X. F. [1 ]
Xin, L. [1 ]
Shoji, T. [1 ,2 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
[2] Tohoku Univ, New Ind Creat Hatchery Ctr, Frontier Res Initiat, 6-6-10 Aramaki Aoba,Aoba Ku, Sendai, Miyagi 9808579, Japan
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Inconel; 690; TT; Impact fretting corrosion; Oxidation; Microstructure; SURFACE OXIDE-FILMS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; NANOLAMINATED STRUCTURE; ALLOY; 690TT; DEFORMATION; TUBES; SUPERALLOY; EVOLUTION; DIFFUSION;
D O I：
10.1016/j.corsci.2024.112507
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The impact fretting corrosion of Inconel 690TT under different impact forces was investigated. The results indicated that there was a competitive relationship between formation of third body layer (TBL) and fragmentation of TBL caused by impact force. With the increase of impact forces, damage mechanism changed from adhesive wear to delamination wear, and crack initiation sites gradually shifted from TBL to internal oxidation zone in tribologically transformed structure (TTS) layer. Nanocrystalline boundaries and defects induced by impact force provided channels for internal oxidation. The formation mechanism of TTS was the combined effect of continuous dynamic recrystallization (cDRX) and twin-assisted cDRX.
引用
收藏
页数：19
相关论文
共 45 条
  • [21] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water
    Xing-Chen Liu
    Hong-Liang Ming
    Zhi-Ming Zhang
    Jian-Qiu Wang
    Li-Chen Tang
    Hao Qian
    Yong-Cheng Xie
    En-Hou Han
    Acta Metallurgica Sinica(English Letters), 2019, 32 (12) : 1437 - 1448
  • [22] The role of frequency on fretting corrosion of Alloy 690TT against 304 stainless steel in high temperature high pressure water
    Xin, L.
    Lu, Y. H.
    Otsuka, Y.
    Mutoh, Y.
    Wang, Z. H.
    Shoji, T.
    MATERIALS CHARACTERIZATION, 2017, 134 : 260 - 273
  • [23] Cyclic deformation behavior and cracking mechanism of Inconel Alloy 690TT steam generator tube at elevated temperature
    Li, Z. H.
    Hong, C.
    Zhao, Y. G.
    Hu, Y.
    Lu, Y. H.
    Shoji, T.
    MATERIALS CHARACTERIZATION, 2022, 190
  • [24] Effect of normal force on the fretting wear behavior of Inconel 690 TT against 304 stainless steel in simulated secondary water of pressurized water reactor
    Ming, Hongliang
    Liu, Xingchen
    Zhang, Zhiming
    Wang, Jianqiu
    Hana, En-Hou
    TRIBOLOGY INTERNATIONAL, 2018, 126 : 133 - 143
  • [25] Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water
    Long Xin
    Yongming Han
    Ligong Ling
    Yonghao Lu
    Tetsuo Shoji
    Acta Metallurgica Sinica (English Letters), 2021, 34 : 543 - 554
  • [26] Microstructure Evolution of 690 TT Heat Transfer Tube Under Impact Slip Dual-Axis Fretting Corrosion in High Temperature and High Pressure Water Environment
    Zhou, Bokai
    Liu, Xin
    Li, Shen
    Hu, Yong
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (08) : 2156 - 2166
  • [27] Impact-sliding fretting tribo-corrosion behaviors of Inconel 690 alloy pretreated with HTHP immersion for different durations
    Wang, Guoping
    Xiong, Hailong
    Zhou, Sijia
    Yin, Meigui
    TRIBOLOGY INTERNATIONAL, 2025, 204
  • [28] The synergy of corrosion and fretting wear process on Inconel 690 in the high temperature high pressure water environment
    Wang, Zihao
    Xu, Jian
    Li, Jie
    Xin, Long
    Lu, Yonghao
    Shoji, Tetsuo
    Takeda, Yoichi
    Otsuka, Yuichi
    Mutoh, Yoshiharu
    JOURNAL OF NUCLEAR MATERIALS, 2018, 502 : 255 - 262
  • [29] Investigation into the fretting corrosion of alloy 690 TT against type 304 stainless steel in high temperature pure water under partial slip conditions
    Xin, Long
    Liang, Xue
    Han, Yongming
    Lu, Yonghao
    Shoji, Tetsuo
    TRIBOLOGY INTERNATIONAL, 2019, 134 : 93 - 101
  • [30] Effects of foreign object damage on high-cycle fatigue behavior of Inconel Alloy 690TT steam generator tubes
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Zhang, W. D.
    Shoji, T.
    ENGINEERING FRACTURE MECHANICS, 2023, 292
12345