Effect of porous C/C substrate density on compressive property of C/C-Cu composites

被引:0
|
作者
机构
[1] Yin, Jian
[2] Zhang, Hong-Bo
[3] Xiong, Xiang
[4] Tan, Cui
[5] Lu, Cai-Tao
来源
Yin, Jian | 1600年 / Central South University卷 / 19期
关键词
C/C composites - Carbon fiber reinforced carbon - Compressive properties - Different densities - Porous carbon/carbon composites - Substrate density - Tensile testing machines - Vertical direction;
D O I
暂无
中图分类号
学科分类号
摘要
Carbon fiber reinforced carbon and copper (C/C-Cu) composites were prepared by a combination of chemical vapor infiltration (CVI) and melt copper impregnation by pressure. 3 kinds of C/C-Cu composites with different densities of porous carbon/carbon composites (C/C substrates) were prepared and their compressive properties were tested on CSS-44100 electronic tensile testing machine. The effect of C/C substrate density on compressive property of C/C-Cu composites was studied. The results show that C/C-Cu composites have high compressive strengths, which have small differences between parallel and vertical direction. With the increase of the C/C substrate density, the compressive strength of C/C-Cu composites increases and the anisotropy improves. The one with highest density has the highest compressive strength of 323.8 and 326.6 MPa. The composites are shearing along with 45° diagonal line in vertical direction, while destroyed by delaminating split in parallel direction.
引用
收藏
相关论文
共 50 条
  • [41] C/C-Cu复合材料的微观结构与冲击性能
    谭翠
    张红波
    尹健
    粉末冶金材料科学与工程, 2013, 18 (03) : 441 - 446
  • [42] C/C-Cu复合材料的载流摩擦磨损行为
    杨琳
    易茂中
    冉丽萍
    中国有色金属学报, 2009, 19 (09) : 1613 - 1617
  • [43] Evaluation of the coating layer formed on the substrate of C/C composites
    Kachi, T
    Kato, Y
    Ushigome, N
    Arai, N
    ENERGY CONVERSION AND MANAGEMENT, 2001, 42 (15-17) : 1963 - 1975
  • [44] The observation of collective effects in central C-Ne and C-Cu collisions at a momentum of 4.5 GeV/c per nucleon
    Chkhaidze, L
    Djobava, T
    Gogiberidze, G
    Kharkhelauri, L
    PHYSICS LETTERS B, 1997, 411 (1-2) : 26 - 32
  • [45] Evolution of porous structure and fatigue behavior of C/C composites
    Liao, Xiaoling
    Xu, Wenfeng
    Li, Hejun
    FRACTURE AND DAMAGE MECHANICS V, PTS 1 AND 2, 2006, 324-325 : 599 - +
  • [46] Effect of the Ti content of Cu-Ti alloy on the wettability of C/C composites
    Zhang, F.-Q. (zhang_fuqin01@yahoo.com.cn), 1600, Central South University, Lushan Nanlu, Changsha, 410043, China (18):
  • [47] Tensile strength and fracture toughness of C/C and metal infiltrated composites Si-C/C and Cu-C/C
    Wang, Wen-Xue
    Takao, Yoshihiro
    Matsubara, Terutake
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2008, 39 (02) : 231 - 242
  • [48] Effect of carbon fiber preform with variable density on the oxidation behavior of C/C composites
    Lu, Xuefeng
    Zhang, Jie
    Qian, Kun
    Cao, Haijian
    Yu, Kejing
    Sun, Jie
    Gongneng Cailiao/Journal of Functional Materials, 2015, 46 (17): : 17042 - 17045
  • [49] Improvement of the Photoelectrochemical Stability of Cu2O Photocathode by Ph-C(sic)C-Cu Grafting
    Zhang, Wen
    Bai, Yadi
    Tian, Meng
    Liu, Ya-Ge
    Hou, Jiawei
    Li, Chengbo
    Jiang, Hai-Ying
    Tang, Junwang
    ADVANCED MATERIALS INTERFACES, 2023, 10 (03)
  • [50] Efficiently elimination of high concentration dye pollutants by Ph-C=C-Cu/ nanoparticles hybrids
    Hou, Jiawei
    Tian, Meng
    Bai, Yadi
    Qian, Jing
    Liu, Ya-Ge
    Jing, Biyun
    Jia, Yibing
    Jiang, Hai-Ying
    JOURNAL OF WATER PROCESS ENGINEERING, 2023, 55