Synthesis and thermal properties of nanocomposites based on exfoliated organoclay polystyrene and poly(methylmethacrylate)

被引：16

作者：

Akelah A. ^{[1
]}

Rehab A. ^{[1
]}

Abdelwahab M. ^{[1
]}

Betiha M.A. ^{[2
]}

机构：

[1] Polymer Research Group, Chemistry Department, Faculty of Science, Tanta University, Tanta

[2] Egyptian Petroleum Research Institute, Cairo

来源：

Nanocomposites | 2017年 / 3卷 / 01期

关键词：

Clay-polymer hybrids; Exfoliated montmorillonite; Intercalated clay-polymer; Nanocomposites; Polymer-MMT materials;

D O I：

10.1080/20550324.2017.1316599

中图分类号：

学科分类号：

摘要：

Exfoliated organoclay-polystyrene (OC-PS) and organoclay-poly(methyl methacrylate) (OC-PMMA) nanocomposites were prepared using novel modified/clay-polymer through both bulk polymerization and solution techniques. The synthesis was achieved by formation of derivative vinylbenzyl ammonium salt intercalated with montmorillonite (MMT) clay. The clay-vinyl/monomer was dispersed in PS or MMA monomers followed by solution polymerization. The clay-PS and clay-PMMA were used as highly compatibilizer organoclay to produce highly exfoliated nanocomposites. Morphological structure of the nanocomposites was investigated by SEM and XRD which confirmed that the clay is homogenously dispersed and exfoliated in the polymer matrixes with interlayer spacing at least of d001-value ≥4 nm for both PS and PMMA. Thermal properties of the nanocomposites show an increase in the decomposition temperature comparing to neat polymer. © 2017, © 2017 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group.

引用

页码：20 / 29

页数：9

共 29 条

[1]

Alexandre M., Dubois P., Polymer-layered silicate nanocomposites: preparation, properties and uses of a new class of materials, Mater. Sci. Eng. R: Rep., 28, 1-2, pp. 1-63, (2000)

[2]

Su S., Jiang D.D., Wilkie C.A., Methacrylate modified clays and their polystyrene and poly(methyl methacrylate) nanocomposites, Polym. Adv. Technol, 15, 5, pp. 225-231, (2004)

[3]

Fu X., Qutubuddin S., Polymer–clay nanocomposites: exfoliation of organophilic montmorillonite nanolayers in polystyrene, Polymer, 42, 2, pp. 807-813, (2001)

[4]

Huskic M., Zigon M., Ivankovic M., Comparison of the properties of clay polymer nanocomposites prepared by montmorillonite modified by silane and by quaternary ammonium salts, Appl. Clay Sci., 85, pp. 109-115, (2013)

[5]

Rehab A., Akelah A., Agag T., Betiha M., Polymer–organoclay hybrids by polymerization into montmorillonite-vinyl monomer interlayers, J. Appl. Polym. Sci., 106, 5, pp. 3502-3514, (2007)

[6]

Xiao J., Wang S., Lu P., Hu Y., Effect of organically modified montmorillonite on thermal degradation mechanism of polycarbonate nanocomposites, Procedia Eng, 62, pp. 791-796, (2013)

[7]

Gu Z., Gao L., Song G., Liu W., Li P., Shan C., Octadecylammonium montmorillonite/natural rubber/cis-1,4-polybutadiene nanocomposites, Appl. Clay Sci., 50, 1, pp. 143-147, (2010)

[8]

Giannakas A., Spanos C.G., Kourkoumelis N., Vaimakis T., Ladavos A., Preparation, characterization and water barrier properties of PS/organo-montmorillonite nanocomposites, Eur. Polym. J., 44, 12, pp. 3915-3921, (2008)

[9]

Gilman J.W., Jackson C.L., Morgan A.B., Harris R., Manias E., Giannelis E.P., Wuthenow M., Hilton D., Phillips S.H., Flammability properties of polymer-layered-silicate nanocomposites. Polypropylene and polystyrene nanocomposites†, Chem. Mater., 12, 7, pp. 1866-1873, (2000)

[10]

Wang J., Du J., Zhu J., Wilkie C.A., An XPS study of the thermal degradation and flame retardant mechanism of polystyrene-clay nanocomposites, Polym. Degrad. Stab., 77, 2, pp. 249-252, (2002)

← 1 2 3 →