Damage behavior and mechanical property investigation of CFRP/CFRP washer-bushing riveted joints

被引：1
|
作者：
Zhao L. [1 ]
Yang T. [1 ]
Huang Q. [1 ]
Zuo Y. [1 ]
机构：
[1] School of Aeronautics and Astronautics, Sichuan University, Chengdu
来源：
Xibei Gongye Daxue Xuebao/Journal of Northwestern Polytechnical University | 2023年 / 41卷 / 06期
关键词：
composites; damage; failure; pull-off property; riveting; shear property;
D O I：
10.1051/jnwpu/20234161089
中图分类号：
学科分类号：
摘要：
Carbon fiber reinforced composites (CFRP) are prone to occur riveting damage. Therefore, the damage behaviors and mechanical properties of CFRP / CFRP washer-bushing riveted joints were investigated experimentally in this paper. Results showed that due to the uneven expansion of rivet shank and local pressure caused by upsetting head, CFRP / CFRP riveted joints occurred multiple damage modes by using net riveting method and bushing method. The damage was mainly located in the layer around the CFRP hole near the upsetting head. However, washer-bushing riveting method effectively limited the uneven expansion and the local pressure of upsetting head, and no obvious damage was observed. Load-displacement curves of direct riveted joints and washer-bushing riveted joints exhibited obvious linear stage, progressive damage stage and final failure stage in both tensile shear and pull-off tests. However, the bushing reduced the effective fastening area of upsetting head, and load-displacement curves of bushing riveted joints only included linear and failure stages. Besides, the tensile shear and pull-off peak load were also the lowest. Tensile failure modes of both net riveted joints and washer-bushing riveted joints were dominated by the coupling failure mode of shear failure and rivet pull-off. The CFRP connecting hole was observed with obvious shear damage and extrusion deformation area. Besides, pull-off failure modes were laminate fracture and ply delamination, and also accompanied by laminate bending deformation. In contrast, bushing riveted joints failed by rivet pull-off in both tensile shear and pull-off tests. ©2023 Journal of Northwestern Polytechnical University.
引用
收藏
页码：1089 / 1096
页数：7
相关论文
共 16 条
  • [1] YANG G, YANG T, YUAN W, Et al., The influence of surface treatment on the tensile properties of carbon fiber-reinforced epoxy composites-bonded joints, Composites Part B: Engineering, 160, pp. 446-456, (2019)
  • [2] XIONG Jian, LI Zhibin, LIU Huibin, Et al., Advances in aerospace lightweight composite shell structure, Acta Materiae Compositae Sinica, 38, 6, pp. 1629-1650, (2021)
  • [3] LEED W, SONG J I., Research on simple joint method using fiber-metal laminate design for improved mechanical properties of CFRP assembly structure, Composites Part B: Engineering, 164, pp. 358-367, (2019)
  • [4] THOPPUL S D, FINEGAN J, GIBSON R F., Mechanics of mechanically fastened joints in polymer-matrix composite structures-a review, Composites Science and Technology, 69, 3, pp. 301-329, (2009)
  • [5] LI Yongbing, MA Yunwu, LOU Ming, Et al., Advances in spot joining technologies of lightweight thin-walled structures, Journal of Mechanical Engineering, 56, 6, pp. 125-146, (2020)
  • [6] HOU Chi, WAN Xiaopeng, HUANG Heyuan, Et al., Fastener connection flexibility of multi-bolted joint of composite laminate, Acta Aeronautica et Astronautica Sinica, 39, 3, (2018)
  • [7] ZHANG Dawei, ZHANG Qi, FAN Xiaoguang, Et al., Review on joining process of carbon fiber-reinforced polymer and metal: methods and joining process, Rare Metal Materials and Engineering, 47, 12, pp. 3686-3696, (2018)
  • [8] MUND M, LIPPKY K, BLASS D, Et al., Influence of production based surface topography and release agent amount on bonding properties of CFRP, Composite Structures, 216, 5, pp. 104-111, (2019)
  • [9] WEI Jingchao, JIAO Guiqiong, YAN Zhaoming, Et al., Bearing strength of composite joints interference-fitted with blind bolts, Acta Aeronautica et Astronautica Sinica, 34, 7, pp. 1627-1635, (2013)
  • [10] CAO Zengqiang, ZUO Yangjie, Electromagnetic riveting technique and its applications, Chinese Journal of Aeronautics, 33, 1, pp. 5-15, (2020)
12