Effect of post-weld heat treatment on the wear resistance of hardfacing martensitic steel deposits

被引：1

作者：

Gualco A. ^{[1
]}

Svoboda H.G. ^{[2
]}

Surian E.S. ^{[1
,3
]}

de Vedia L.A. ^{[4
]}

机构：

[1] Faculty of Engineering, Universidad Nacional de Lomas de Zamora, Buenos Aires

[2] Materials and Structures Laboratory, Faculty of Engineering, Conicet, Universidad de Buenos Aires, Buenos Aires

[3] Deytema-Centre for Materials Development and Technology, Regional Faculty of San Nicolás, Universidad Tecnológica Nacional, Buenos Aires

[4] Institute of Technology Professor J. A. Sábato, Universidad Nacional de San Martín-CNEA, CIC, Buenos Aires

来源：

Welding International | 2010年 / 24卷 / 04期

关键词：

AMSLER wear test; Hardfacing; Martensite; Post-weld heat treatment;

D O I：

10.1080/09507110902844071

中图分类号：

学科分类号：

摘要：

The effect of different post-weld heat treatments on the microstructure and wear resistance of martensitic deposits were studied. The deposit was welded using a metal-cored tubular wire, in the flat welding position, on a 375 × 75 × 19mm SAE 1010 plate, using 98% Ar-2% CO2 shielding gas mixture and with an average heat input of 2.8 kJ/mm. The samples were heat treated at temperatures between 500 and 6808C for 2 h. Chemical composition, Vicker's microhardness and wear properties with AMSLER tests in a sliding condition were determined. In the as welded condition, the microstructure was principally composed of martensite and retained austenite. Significant variations in wear resistance and hardness were measured for different tempering temperatures. For the different heat-treated conditions, it was observed that the decomposition of retained austenite to martensite and carbide precipitation was associated with the tempering of martensite. A secondary hardness effect was detected with maximum hardness of 710HV for 550°C heat treatment temperature. The best performance in wear test was obtained for this condition. Wear rates for the different conditions were obtained and mathematical expressions were developed. For each case, wear mechanisms were analyzed. © 2010 Taylor & Francis.

引用

页码：258 / 265

页数：7

共 26 条

[1]

Merric S., Kotecki D., Wu J., Surfacing. Welding Handbook: Materials and Applications, 4, pp. 392-435, (1998)

[2]

Bhushan B., Gupta B.K., Handbook of Tribology: Materials, Coating, and Surface Treatment, (1997)

[3]

Huisman M.D., Flux-and metal-cored wires, a productive alternative to stick electrodes and solid wires, Svetsaren, 51, 1-2, pp. 6-14, (1996)

[4]

Lyttle K.A., Metal cored wires: Where do they fit in your future?, Weld J, 75, 10, pp. 35-38, (1996)

[5]

Myers D., Metal cored wires: Advantages and disadvantages, Weld J, 81, 9, pp. 39-42, (2002)

[6]

Wu W., Hwu L.Y., Lin D.Y., Lee J.L., The relationship between alloying elements and retained austenite in martensitic stainless steel welds, Scripta Materialia, 42, pp. 1071-1076, (2000)

[7]

Kotecki D., Ogborn J., Abrasion resistance of iron-based hardfacing alloys, Weld J, 74, 8, pp. 269-278, (1995)

[8]

Bortoni O.E., Patrone J.J., Marino P.S., Recargues por soldadura de superficies sometidas a desgaste, Siderurgia, 49, pp. 114-139, (1989)

[9]

Hoja de producto: EnDOtec DO15, (1996)

[10]

ASM Handbook: Mechanical Testing and Evaluation, 8, pp. 751-755, (2003)