Insight into SO2 poisoning mechanism of MnOx-CeO2/Ti-bearing blast furnace slag catalyst for low temperature NH3-SCR reaction

被引:0
作者
Kong, Ming [1 ]
Liao, Heping [1 ]
Song, Linjiang [1 ]
Zhang, Shengchao [1 ]
Wang, Yunchuan [1 ]
Feng, Wei [1 ]
Liu, Zhifang [1 ]
Deng, Xianling [1 ]
Yao, Lu [2 ]
Zhang, Handan [3 ]
机构
[1] Chongqing Univ Sci & Technol, Sch Mech & Intelligent Mfg, Chongqing 401331, Peoples R China
[2] Chongqing Univ Posts & Telecommun, Sch Sci, Chongqing 400065, Peoples R China
[3] Xi An Jiao Tong Univ, Inst Polymer Sci Chem Engn, Sch Chem Engn & Technol, Shaanxi Key Lab Energy Chem Proc Intensificat, Xian 710049, Shaanxi, Peoples R China
基金
中国国家自然科学基金;
关键词
MnO x -C e O 2 catalyst; Ti-bearing blast furnace slag; NH3-SCR; SO2poisoningmechanism; OXIDE-BASED CATALYSTS; REDUCTION; NO; SCR; NH3; RESISTANCE; REMOVAL; REGENERATION; TOLERANCE; TIO2;
D O I
10.1016/j.mcat.2024.114609
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Sulfur poisoning is an intractable challenge for NH3-SCR catalyst. In this issue, the immanent reasons for MnOx- CeO2/Ti-bearing blast furnace slag catalyst deactivation resulting from SO2 were elaborated by catalytic activity evaluation, BET, XRD, XPS, NH3-TPD, H2-TPR and in-situ DRIFTS analysis. Results showed that MnOx-CeO2/Ti- bearing blast furnace slag catalyst followed E-R reaction mechanism and performed 100 % NO conversion at 175 degrees C, whereas its sulfur resistance was unsatisfactory and the deactivation degree became more severe with SO2 concentration increasing. SO2 reacted with NH3 to generate (NH4)2SO4 and NH4HSO4 deposits, blocking catalyst pores and covering active sites. SO2 also interacted with MnOx-CeO2 active components to form MnSO4 and Ce2(SO4)3, which restricted the electron transfers of Mn4+/Mnn+ and Ce3+/Ce4+. Besides, the newly formed sulfur-containing acidic sites also competed with the original active sites for NH3 adsorption, thereby hindering the SCR reaction. Physical purging could not realize regeneration of SO2-poisoning catalyst, but hyperthermic treatment was an efficient solution.
引用
收藏
页数:12
相关论文
共 50 条
[41]   Influence of Mn/Ce ratio on the physicochemical properties and catalytic performance of graphene supported MnOx-CeO2 oxides for NH3-SCR at low temperature [J].
You, Xiaochen ;
Sheng, Zhongyi ;
Yu, Danqing ;
Yang, Liu ;
Xiao, Xiang ;
Wang, Sheng .
APPLIED SURFACE SCIENCE, 2017, 423 :845-854
[42]   Deactivation and Regeneration for the SO2-Poisoning of a Cu-SSZ-13 Catalyst in the NH3-SCR Reaction [J].
Wang, Yan ;
Li, Zhaoqiang ;
Fan, Rongrong ;
Guo, Xin ;
Zhang, Cheng ;
Wang, Yu ;
Ding, Zhiyong ;
Wang, Rong ;
Liu, Wei .
CATALYSTS, 2019, 9 (10)
[43]   Low-Cost CuX Catalyst from Blast Furnace Slag Waste for Low-Temperature NH3-SCR: Nature of Cu Active Sites and Influence of SO2/H2O [J].
Chen, Lin ;
Ren, Shan ;
Xing, Xiangdong ;
Yang, Jie ;
Yang, Jian ;
Wang, Mingming ;
Chen, Zhichao ;
Liu, Qingcai .
ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2022, 10 (23) :7739-7751
[44]   Enhancing the K-poisoning resistance of CeO2-SnO2 catalyst by hydrothermal method for NH3-SCR reaction [J].
Zhao, Wanxia ;
Rong, Jing ;
Luo, Wen ;
Long, Lulu ;
Yao, Xiaojiang .
APPLIED SURFACE SCIENCE, 2022, 579
[45]   Excellent operating temperature window and H2O/SO2 resistances of Fe-Ce catalyst modified by different sulfation strategies for NH3-SCR reaction [J].
Wang, Xiaobo ;
Guo, Ning ;
Peng, Jiaqi ;
Wang, Yue ;
Li, Haijie ;
Ren, Dongdong ;
Gui, Keting .
ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH, 2023, 30 (17) :50635-50648
[46]   The combination effects of K2O and PbO poisoning on NH3-SCR TiO2-CeO2 catalyst [J].
Cao, Jun ;
Lu, Zhuquan ;
Teng, Liumei ;
Qiao, Xu ;
Liu, Weizao ;
Wu, Hongli ;
Jiang, Lijun ;
Wu, Qirong ;
Liu, Qingcai .
JOURNAL OF ENVIRONMENTAL CHEMICAL ENGINEERING, 2021, 9 (05)
[47]   The effect of SO2 on NH3-SCR reaction synergistic CO oxidation over a Mn-Co-Ti catalyst [J].
Liang, Quanming ;
Tong, Li ;
Liu, Jieyu ;
Dan, Mo ;
Chen, Ke .
APPLIED CATALYSIS O: OPEN, 2024, 194
[48]   Promoted performance of a MnOx/PG catalyst for low-temperature SCR against SO2 poisoning by addition of cerium oxide [J].
Zhang, Lianfeng ;
Zhang, Xianlong ;
Lv, Shuangshuang ;
Wu, Xueping ;
Wang, PeiMeng .
RSC ADVANCES, 2015, 5 (101) :82952-82959
[49]   Insight into SO2 poisoning over Cu-SAPO-18 used for NH3-SCR [J].
Ming, Shujun ;
Pang, Lei ;
Chen, Zhen ;
Guo, Yanbing ;
Guo, Lei ;
Liu, Qian ;
Liu, Peng ;
Dong, Yahao ;
Zhang, Shoute ;
Li, Tao .
MICROPOROUS AND MESOPOROUS MATERIALS, 2020, 303
[50]   Facile Preparation of CeO2 Supported on Graphene Oxide Sheets for NH3-SCR: Improvement of Catalytic Activity and SO2 Tolerance [J].
Zhou, Zhiyuan ;
Wang, Yongzhao ;
Yuan, Qunfu ;
Guo, Yanle ;
Guo, Wenyao ;
Xin, Zhiling ;
Zhang, Bingsen ;
Guo, Ruitang .
CHEMISTRYSELECT, 2021, 6 (19) :4859-4865