Preparation and characterization of sodium-graphite intercalation compounds

被引：0

作者：

Akuzawa, Noboru ^{[1
]}

Yoshioka, Jun ^{[1
]}

Ozaki, Chihiro ^{[2
]}

Tokuda, Masahide ^{[2
]}

Ohkura, Kenji ^{[2
]}

Soneda, Yasushi ^{[3
]}

机构：

[1] Tokyo National College of Technology, 1220-2 Kunugida, Tokyo, Hachioji,193-0997, Japan

[2] SEC Corporation, 3-26 Osadano, Kyoto, Fukuchiyama,620-0853, Japan

[3] National Institute of Advanced Industrial Science and Technology (AIST), 16-1 Onogawa, Ibaraki, Tsukuba,305-8569, Japan

来源：

Molecular Crystals and Liquid Crystals | 2002年 / 388卷 / 01期

关键词：

Alkali metal-graphite intercalation compounds - G-values - Metallic temperature dependence;

D O I：

10.1080/10587250215260

中图分类号：

学科分类号：

摘要：

Preparation and characterization of sodium-graphite intercalation compounds were investigated. It was confirmed that the resulting compound (NaC x) had the stage 8 structure with identity period of 2.8 nm. The Raman spectroscopy showed that the G-band signal of NaC x was observed at 1582 cm −1 and at 1608 cm −1, which is a typical indication of the formation of intercalation compounds. The g-value of NaC x was determined to be 2.0018 by the ESR measurement, which was very close to the reported values for the other alkali metal-graphite intercalation compounds. The electrical resistivity of NaC x was about 1/3 of that of host graphite at room temperature and showed metallic temperature dependence. © 2002, Copyright Taylor & Francis Group, LLC.

引用

页码：1 / 7

共 50 条

[21] CHARACTERIZATION OF GRAPHITE INTERCALATION COMPOUNDS BY MAGNETIC-RESONANCE
EBERT, LB
BULLETIN OF THE AMERICAN PHYSICAL SOCIETY, 1978, 23 (03): : 185 - 186
[22] CHARACTERIZATION OF GRAPHITE-INTERCALATION COMPOUNDS BY THERMOGRAVIMETRIC ANALYSIS
HOHNE, M
HUMMEL, HJ
WANG, YX
STUMPP, E
THERMOCHIMICA ACTA, 1991, 179 : 201 - 207
[23] Synthesis and Characterization of Graphite Intercalation Compounds with Sulfuric Acid
Rimkute, Gintare
Gudaitis, Mantvydas
Barkauskas, Jurgis
Zarkov, Aleksej
Niaura, Gediminas
Gaidukevic, Justina
CRYSTALS, 2022, 12 (03)
[24] INTERCALATION COMPOUNDS OF GRAPHITE
DRESSELHAUS, MS
DRESSELHAUS, G
ADVANCES IN PHYSICS, 1981, 30 (02) : 139 - 326
[25] GRAPHITE INTERCALATION COMPOUNDS
RUDORFF, W
ADVANCES IN INORGANIC CHEMISTRY, 1959, 1 : 223 - 266
[26] INTERCALATION COMPOUNDS OF GRAPHITE
EBERT, LB
ANNUAL REVIEW OF MATERIALS SCIENCE, 1976, 6 : 181 - 211
[27] BISMUTH(III) CHLORIDE GRAPHITE-INTERCALATION COMPOUNDS - PREPARATION AND CHARACTERIZATION OF THE FIRST STAGE COMPOUND
SCHULZ, F
LOCHTE, K
FROBA, M
METZ, W
MOLECULAR CRYSTALS AND LIQUID CRYSTALS SCIENCE AND TECHNOLOGY SECTION A-MOLECULAR CRYSTALS AND LIQUID CRYSTALS, 1994, 244 : 71 - 76
[28] PREPARATION AND CHARACTERIZATION OF TUNGSTEN-OXIDE FLUORIDE AND TUNGSTEN FLUORIDE GRAPHITE-INTERCALATION COMPOUNDS
NAKAJIMA, T
MOLINIER, M
SYNTHETIC METALS, 1990, 34 (1-3) : 103 - 108
[29] Intercalation compounds of graphite
Dresselhaus, MS
Dresselhaus, G
ADVANCES IN PHYSICS, 2002, 51 (01) : 1 - 186
[30] GRAPHITE INTERCALATION COMPOUNDS
FISCHER, JE
THOMPSON, TE
PHYSICS TODAY, 1978, 31 (07) : 36 - &

← 1 2 3 4 5 →