Effect of austempering temperature on microstructure and properties of austempered ductile iron

被引：0
作者：
Han C.F. [1 ]
Zhou W.Q. [1 ]
Sun Y.F. [1 ]
Ma J.T. [2 ]
机构：
[1] School of Mechanical and Electrical Engineering, Xinlian College of Henan Normal University, No. 50, Zhengkai Road, Zhengdong New District, Zhengzhou City, Henan Province
[2] ABU Quality Department, BYD Company Limited, Huizhou
来源：
International Journal of Microstructure and Materials Properties | 2018年 / 13卷 / 05期
关键词：
Austempered ductile iron; Austempering temperature; Impact toughness; Tensile strength; Wear resistance;
D O I：
10.1504/ijmmp.2018.10018203
中图分类号：
学科分类号：
摘要：
The influence of austempering temperature on microstructure and properties of Austempered Ductile Iron were studied in this paper. The purpose was to improve comprehensive performance of Austempered Ductile Iron for adapting to slurry pump transflux parts. The nodularisation grade of graphite was 2–3 magnitude and the size of graphite was 6–7 magnitude. After austempered at different temperatures for 120 min, the microstructure mainly consisted of acicular ferrite, retained austenite and spheroidal graphite. With increasing austempering temperature, tensile strength improved firstly and then decreased, impact toughness increased, the wear resistance became worse, and the corrosion resistance increased. When the heat treatment process was 900°C × 90 min + 250°C × 120 min，the comprehensive performance was better (tensile strength: 1710 MPa, elongation: 2%, impact toughness: 40 J/cm2, Brinell hardness: 467 HBW, wear weightlessness rate: 0.17 mg/m) than the requirements in ASTM A897-06. Copyright © 2018 Inderscience Enterprises Ltd.
引用
收藏
页码：344 / 357
页数：13
相关论文
共 19 条
  • [1] Azimian M., Bart H.J., Erosion investigations by means of a centrifugal accelerator erosion tester, Wear, 328-329, pp. 249-256, (2015)
  • [2] Basso D., Martinez R.A., Sikora J.A., Influence of austenitising and austempering temperatures on microstructure and properties of dual phase ADI, Mater. Sci. Technol., 23, 11, pp. 1321-1326, (2013)
  • [3] Bassoa D., Martineza R., Sikoraa J., Influence of section size on dual phase ADI microstructure and properties: Comparison with fully ferritic and fully ausferritic matrices, Mater. Sci. Technol., 25, 10, pp. 1271-1278, (2009)
  • [4] Batra U., Ray S., Prabhakar S.R., Impact properties of copper-alloyed and nickel-copper alloyed ADI, J. Mater. Eng. Performm, 16, 4, pp. 485-489, (2007)
  • [5] Benam S., Effect of alloying elements on austempered ductile iron (ADI) properties and its process: Review, Chin. Foundry, 12, 1, pp. 54-70, (2015)
  • [6] Metallic Materials–Wear Test Method– Block-on-Ring Sliding Wear Test, (2006)
  • [7] Austempered Ductile Iron (ADI) Castings, (2009)
  • [8] Metallographic Test for Spheroidal Graphite Cast Iron, (2009)
  • [9] Gietka T., Ciechacki K., Modeling of railway wheels made of austempered ductile iron, Arch. Metall. Mater., 61, 4, pp. 1833-1838, (2016)
  • [10] Han F., Sun Y.F., Wu Y., Ma Y.H., Effects of vanadium and austempering temperature on microstructure and properties of CADI, Metallogr. Microstruct. Anal., 4, 3, pp. 135-145, (2015)
12