TOF-SIMS analysis of the bleeding of organic compounds to pulp fiber surface

被引：0
|
作者：
Higashi, Hiroto [1 ]
Nakamura, Toko [1 ]
Ornatsu, Masayuki [1 ]
机构：
[1] Material Analysis Center, Oji Paper Co.
来源：
Kami Pa Gikyoshi/Japan Tappi Journal | 2008年 / 62卷 / 02期
关键词：
Bleeding; Pulp; Surface analysis; TOF-SIMS; XPS;
D O I：
10.2524/jtappij.62.196
中图分类号：
学科分类号：
摘要：
It was commonly found that the aging and the manufacturing conditions were influenced on the surface properties of the paper. We assumed that the change of the surface properties was caused by the bleeding of the low-molecular-mass compounds to pulp fiber surface. In order to confirm this assumption we carried out the surface analysis of handsheets using XPS and TOF-SIMS. A handsheet was prepared from a hardwood pulp. TOF-SIMS and XPS analysis showed that the bleedable compounds, such as C-C chemical bonds increase on the surface of the sheet at high temperature.
引用
收藏
页码：82 / 86
页数：4
相关论文
共 50 条
  • [11] Advances in the surface characterization of heterogeneous catalysts using ToF-SIMS
    Weng, Lu-Tao
    APPLIED CATALYSIS A-GENERAL, 2014, 474 : 203 - 210
  • [12] A comparative study on detection of organic surface modifiers on mineral grains by TOF-SIMS, VUVSALI TOF-SIMS and VUVSALI with laser desorption
    Dimov, SS
    Chryssoulis, SL
    APPLIED SURFACE SCIENCE, 2004, 231 : 528 - 532
  • [13] ToF-SIMS and SEM-EDS analysis of the surface of chosen bioindicators
    Szynkowska, M. I.
    Pawlaczyk, A.
    Rogowski, J.
    APPLIED SURFACE SCIENCE, 2008, 255 (04) : 1165 - 1169
  • [14] Analysis of the surface chemistry of oxidized polyethylene: comparison of XPS and ToF-SIMS
    Briggs, D
    Brewis, DM
    Dahm, RH
    Fletcher, IW
    SURFACE AND INTERFACE ANALYSIS, 2003, 35 (02) : 156 - 167
  • [15] Application of ToF-SIMS surface analysis to tribochemistry in metal forming processes
    Dauchot, G
    De Castro, E
    Repoux, M
    Combarieu, R
    Montmitonnet, P
    Delamare, F
    WEAR, 2006, 260 (03) : 296 - 304
  • [16] Using ToF-SIMS to study industrial surface phenomena
    Smentkowski, Vincent S.
    Keenan, Michael R.
    Arlinghaus, Henrik
    SURFACE SCIENCE, 2016, 652 : 39 - 45
  • [17] Surface Characterization of Polymer Blends by XPS and ToF-SIMS
    Chan, Chi Ming
    Weng, Lu-Tao
    MATERIALS, 2016, 9 (08)
  • [18] Surface studies of halloysite nanotubes by XPS and ToF-SIMS
    Ng, Kai-Mo
    Lau, Yiu-Ting R.
    Chan, Chi-Ming
    Weng, Lu-Tao
    Wu, Jingshen
    SURFACE AND INTERFACE ANALYSIS, 2011, 43 (04) : 795 - 802
  • [19] The chemical analysis of wood using ToF-SIMS
    Fukushima, Kazuhiko
    Saito, Kaori
    MOKUZAI GAKKAISHI, 2007, 53 (06): : 291 - 297
  • [20] ToF-SIMS analysis of surface-anchored organometallic clusters
    Li, CX
    Lai, MYD
    Leong, WK
    JOURNAL OF ORGANOMETALLIC CHEMISTRY, 2005, 690 (16) : 3861 - 3863
12345