The ultimate tension state of a pipeline subject to pitting-corrosion

被引：0
|
作者：
Borodachev, N.M. [1 ]
机构：
[1] Kievskij Univ. Grazhd. Aviatsii, Kiev, Ukraine
来源：
| 2002年 / Institut Problem Prochnosti NAN卷
关键词：
Numerical analysis - Pitting - Pressure effects - Steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A method is proposed of determining the ultimate state of a pipeline, which is under internal pressure and subjected to pitting-corrosion. A numerical example is considered.
引用
收藏
相关论文
共 50 条
  • [31] A parametric study on effects of pitting corrosion on steel plate's ultimate strength
    Feng, Liang
    He, Jingke
    Hu, Luocun
    Shi, Hongda
    Yu, Changli
    Wang, Shuqing
    Yang, Shuo
    APPLIED OCEAN RESEARCH, 2020, 95
  • [32] Nondestructive Testing of the State of Surfaces Damaged by Corrosion Pitting
    Rusyn, B. P.
    Anufrieva, N. P.
    Hrabovs'ka, N. R.
    Ivanyuk, V. H.
    MATERIALS SCIENCE, 2014, 49 (04) : 516 - 524
  • [33] Ultimate Bending Capacity of Subsea Pipeline with Corrosion-dent Defects
    Hou, Fuheng
    Chen, Yanfei
    He, Guoyan
    Liu, Yu
    Wang, Zhihao
    Wu, Zuming
    Ship Building of China, 2023, 64 (06) : 24 - 34
  • [34] Nondestructive Testing of the State of Surfaces Damaged by Corrosion Pitting
    B. P. Rusyn
    N. P. Anufrieva
    N. R. Hrabovs’ka
    V. H. Ivanyuk
    Materials Science, 2014, 49 : 516 - 524
  • [35] Ultimate load capacity of offshore pipeline with arbitrary shape corrosion defects
    Chen Yan-fei
    Zhang Juan
    Zhang Hong
    Liu Xiao-ben
    Li Xin
    Zhou Jing
    Cao Jing
    CHINA OCEAN ENGINEERING, 2015, 29 (02) : 241 - 252
  • [36] Ultimate Load Capacity of Offshore Pipeline with Arbitrary Shape Corrosion Defects
    陈严飞
    张娟
    张宏
    刘啸奔
    李昕
    周晶
    曹静
    China Ocean Engineering, 2015, 29 (02) : 241 - 252
  • [37] Ultimate load capacity of offshore pipeline with arbitrary shape corrosion defects
    Yan-fei Chen
    Juan Zhang
    Hong Zhang
    Xiao-ben Liu
    Xin Li
    Jing Zhou
    Jing Cao
    China Ocean Engineering, 2015, 29 : 241 - 252
  • [38] Numerical simulation and experimental verification of pitting corrosion propagation in sweet pipeline service 
    Zhu, Zhenjin
    Teevens, Patrick J.
    Xue, Huibin
    Cheng, Y. Frank
    JOURNAL OF PIPELINE SCIENCE AND ENGINEERING, 2022, 2 (01): : 78 - 86
  • [39] Numerical modelling of strength degradation in a steel submarine pipeline subjected to the pitting corrosion
    Magda, W
    PROCEEDINGS OF THE SIXTH (1996) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL II, 1996, 1996, : 469 - 476
  • [40] Understand the occurrence of pitting corrosion of pipeline carbon steel under cathodic polarization
    Liu, Z. Y.
    Li, X. G.
    Cheng, Y. F.
    ELECTROCHIMICA ACTA, 2012, 60 : 259 - 263
12345