Improvement of durability for phosphorus adsorbent fabricated from waste gypsum board by PVB(Polyvinyl Butyral) coating

被引：0
作者：
Yabe H. [1 ]
Shiomi H. [1 ]
机构：
[1] Dept. Chem. and Mater. Tech., Kyoto Inst.of Tech., Sakyo-ku, Kyoto
来源：
Zairyo/Journal of the Society of Materials Science, Japan | 2017年 / 66卷 / 06期
关键词：
Carbonation; Coating; Crystallization; Gypsum board; Phosphorous adsorbent; Polyvinyl butyral;
D O I：
10.2472/jsms.66.393
中图分类号：
学科分类号：
摘要：
From a viewpoint of creation of a recycling society, it is essential to establish a method for recycling waste gypsum boards because large amount of gypsum board are scrapped with rehabilitation of architectural structure. For this purpose, we tried to reuse gypsum boards as phosphorus adsorbents and reported that carbonation of gypsum boards was effective method for the preparation of phosphorus adsorbents with high performance. However, the surface layers of carbonated gypsum boards were easy to peel out after immersion in a phosphorus solution due to the dissolution of gypsum. In this study, aiming at improving the durability of the phosphorus adsorbent we attempted to coat the surface of gypsum boards with PVB(Polyvinyl Butyral) before carbonation. Test pieces cut out from commercial gypsum board were coated PVB by immersing in PVB acetone solution and drying in air. The amount of adhering PVB to the gypsum board increased with increasing PVB concentration. The surfaces of the PVB coated gypsum boards were covered with uniform shaped CaCO3 crystals. Although the PVB coated specimens showed slightly low phosphorus removal ratio in the early stage of phosphorus removal, all samples showed high phosphorus removal ratio more than 90% regardless of PVB coating after 5days immersion. Moreover, although the surface of the samples without PVB coating suffered damage on immersing in the phosphorus solutions, the PVB coated samples kept initial appearance even after long-term immersion in the phosphorus solution. © 2017 The Society of Materials Science, Japan.
引用
收藏
页码：393 / 397
页数：4
相关论文
共 12 条
  • [1] Inamori Y., Kaiqin X.U., Ebie Y., Inamori R., Mizujunkan shakai ni muketa haisui osui shori gijutsu no torikumi, NTS, Haisui Osui Shorigijutsu Shuusei, pp. 3-28, (2007)
  • [2] Kyosai S., Gesui shori to sekkai, Sekkou to Sekkai, 1985, 196, pp. 160-165, (1985)
  • [3] Kozima T., Gesui Shori ni Okeru Shousekihou wo Motiita rin Kaisyuugijutsu no Kaihatsu, pp. 12-20, (2004)
  • [4] Shiomi H., Mukai H., Masui M., Hasidume Y., Akita Y., Development of phosphrous adsorbent using mechanochemically treatd calcium silicate, Journal of the Sciety of Materials Science,Japan, 53, 6, pp. 618-622, (2004)
  • [5] Shirakawa M., Shiomi H., Application of pressurized fluidized bed combustion ash to phosphorous adsorbent, Journal of the Sciety of Materials Science,Japan, 55, 7, pp. 688-692, (2006)
  • [6] Fukui R., Kurahashi T., Shiomi H., Kitaguti S., Shirakawa M., Effect of addition to the gypsum on phosphorous removal propeties of wollastonite-type aszorbent, Journal of the Sciety of Materials Science,Japan, 56, 6, pp. 516-520, (2007)
  • [7] Nitani Y., Shiomi H., Studies on the mechanism of phosphorous removal by crystallization for wallastonite-type adsorbent, Journal of the Sciety of Materials Science,Japan, 61, 6, pp. 500-504, (2012)
  • [8] Murakami K., Sekkou Sekkai Handobukku, pp. 327-330, (1972)
  • [9] Sekkou Bo-Do Hando Bukku Kankyouhen, pp. 195-208, (2012)
  • [10] Kojima Y., Yasue T., Arai Y., Preparation of hardened gypsum body from waste gypsum board, Inorganic Materials, 4, pp. 415-422, (1997)
12