Effects of preparation parameters on microstructure and relative density of copper based composites with large particles of graphite

被引：0

作者：

Zhang M.-J. ^{[1
]}

Liu P.-S. ^{[1
]}

Song S. ^{[1
]}

机构：

[1] Key Laboratory of Beam Technology of Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, Beijing

来源：

Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2022年 / 32卷 / 02期

关键词：

Graphite/copper based composites; Relative density; Structure;

D O I：

10.11817/j.ysxb.1004.0609.2021-37857

中图分类号：

学科分类号：

摘要：

Graphite/copper based composites have good thermal conductivity and lubricity at the same time. In this paper, we try to prepare the graphite/copper based composites with the ultra-large graphite particle size of about 1500 μm, in order to develop a more simple and efficient preparation process and obtain the composites with excellent properties. The effects of different processing parameters on the microstructure and relative density of the composites were investigated for the powder sintering products. The results show that the main factors affecting the microstructure of the composites are the content of graphite and the particle size. The relative density is relatively large for the composites from graphite particle with particle size of 1500 μm, and it can be as high as 0.67 by sintering at 1000 ℃ for 2.5 h. Using graphite particles with smaller particle size, the relative density is relatively small, and it is only 0.43 for the composites from graphite particle with particle size of 120 μm. © 2022, China Science Publishing & Media Ltd. All right reserved.

引用

页码：406 / 415

页数：9

共 21 条

[11]

LI Xiu-hui, YAN Shao-jiu, HONG Qi-hu, Et al., Influence of graphene content on properties of Cu matrix composites, Journal of Materials Engineering, 47, 1, pp. 11-17, (2019)

[12]

LIU Tan, FANG Hua-chan, LI Jin-wei, Et al., Microstructure and properties of pressure-sintered resin carbon-coated graphite/copper composites, The Chinese Journal of Nonferrous Metals, 29, 7, pp. 1446-1456, (2019)

[13]

QIN Xiao, WANG Juan, LIN Gao-yong, Et al., Microstructure, friction and wear properties of copper-coated graphite/copper composites, Materials Reports, 34, pp. 380-384, (2020)

[14]

LIU B, ZHANG D Q, LI X F, Et al., The microstructures and properties of graphite flake/copper composites with high volume fractions of graphite flake, New Carbon Materials, 35, 1, pp. 58-65, (2020)

[15]

HUANG De-bin, LI Chun-sheng, Metal materials handbook, (2005)

[16]

LIN Xue-yang, LIU Ru-tie, XIONG Xiang, Et al., Effects of graphite granularity and pitch binder on properties of copper-graphite brush, The Chinese Journal of Nonferrous Metals, 27, 7, pp. 1411-1418, (2017)

[17]

ZHANG Qin-zhao, LI Qiang, WANG Ai-xiang, Et al., Recent development in copper-graphite self lubrication contact materials, Materials Review, 19, 2, pp. 43-46, (2005)

[18]

ZHU Cheng-cai, ZHANG Peng, DU Yun-hui, Et al., Copper-graphite pantograph slide plate with superexcellent performance, Railway Locomotive & Car, 26, 3, pp. 62-66, (2006)

[19]

LU Ling, ZHU Ding-yi, WANG Cai-liang, Recent development of metal-matrix/graphite solid self-lubricating materials, Materials Review, 21, 2, pp. 38-42, (2007)

[20]

ZHANG Ping, WANG Wen-fang, WU Yu-cheng, Et al., Influence of nano-AlN content on the performance of graphite/Cu-0.6%Cr composites, Materials for Mechanical Engineering, 33, 7, pp. 61-63, (2009)

← 1 2 3 →