Preparation and characterization of ordered mesoporous alumina with high specific surface area with F127 as template

被引：0
作者：
Li, Zhi-Ping
Zhao, Rui-Hong
Guo, Fen
Chen, Jian-Feng
Wang, Gang
机构：
[1] Key Lab for Advanced Preparation Technology and Application with of Nanomaterials, Beijing University of Chemical Technology, Beijing 100029, China
[2] School of Chemistry and Pharmaceutical Engineering, Hebei University of Science and Technology, Shijiazhuang 050018, China
来源：
Gaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities | 2008年 / 29卷 / 01期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Ordered mesoporous alumina was synthesized by sol-gel method with isopropoxide alumina as the source of alumina and PEO-PPO-PEO block copolymer F127 as the template. The results show that the mesoporous alumina surface area (480 m2/g), narrow pore size distribution (2-20 nm), and lange pore volume (over 1.2 cm3/g). Worm-like pore was formed and ordered to some extent. The structure of the synthesized sample was investigated by BET, TEM, and XRD technologies. The influence of various conditions on the structure of ordered mesoporous alumina was discussed.
引用
收藏
页码：13 / 17
相关论文
共 50 条
[31]   Preparation and characterization of high surface area alumina-titania solid acids [J].
Walker, GS ;
Williams, E ;
Bhattacharya, AK .
JOURNAL OF MATERIALS SCIENCE, 1997, 32 (21) :5583-5592
[32]   Preparation and characterization of silica-alumina-pillared montmorilionites with high surface area [J].
Xu Hongyan ;
Bao Xiaojun ;
Wang Tinghai ;
Wang Yonggang .
HIGH-PERFORMANCE CERAMICS V, PTS 1 AND 2, 2008, 368-372 :1712-+
[33]   Preparation and characterization of high surface area alumina-titania solid acids [J].
G. S WALKER ;
E WILLIAMS ;
A. K BHATTACHARYA .
Journal of Materials Science, 1997, 32 :5583-5592
[34]   Preparation and characterization of thermally stable high surface area mesoporous vanadium oxides [J].
Xue, Mingwei ;
Chen, Hui ;
Ge, Jiazhen ;
Shen, Jianyi .
MICROPOROUS AND MESOPOROUS MATERIALS, 2010, 131 (1-3) :37-44
[35]   PREPARATION AND CHARACTERIZATION OF MESOPOROUS, HIGH-SURFACE-AREA ZIRCONIUM(IV) OXIDES [J].
KNOWLES, JA ;
HUDSON, MJ .
JOURNAL OF THE CHEMICAL SOCIETY-CHEMICAL COMMUNICATIONS, 1995, (20) :2083-2084
[36]   Study on the synthesis of ordered mesoporous alumina with high specific surface area using inorganic aluminum sources and its adsorption performance for carbon dioxide [J].
Zhao, Jiasai ;
Zhao, Zhenze ;
Li, Kunjie ;
Zhao, Ruihong ;
Zhao, Huipeng .
MICROPOROUS AND MESOPOROUS MATERIALS, 2024, 377
[37]   IMPROVED PEFORMANCE OF MICRO-PRECONCENTRATOR USING MESOPOROUS SILICA WITH HIGH SPECIFIC SURFACE AREA AS A SURFACE TEMPLATE [J].
Zhao, Bin ;
Feng, Fei ;
Luo, Fan ;
Yang, Xuelei ;
Zhou, Haimei ;
Li, Xinxin .
2019 IEEE 32ND INTERNATIONAL CONFERENCE ON MICRO ELECTRO MECHANICAL SYSTEMS (MEMS), 2019, :472-475
[38]   Preparation of High Specific Surface Area Nano-Alumina by Vacuum Freeze Drying [J].
Liu Xiang-Zhi ;
Piao Ling-Yu ;
Mao Li-Juan ;
Hao Shi-Jie ;
Yang Lei ;
Ju Si-Ting .
ACTA PHYSICO-CHIMICA SINICA, 2010, 26 (04) :1171-1176
[39]   Preparation of Alumina with Large Surface Area and High Thermostability [J].
WANG Junwei TIAN Zhijian XU Jinguang XU Yunpeng XU Zhusheng LIN Liwu Dalian Institute of Chemical Physics The Chinese Academy of Sciences Dalian Liaoning China .
催化学报, 2002, (04) :295-296
[40]   Preparation of alumina with large surface area and high thermostability [J].
Wang, JW ;
Tian, ZJ ;
Xu, JG ;
Xu, YP ;
Xu, ZS ;
Lin, LW .
CHINESE JOURNAL OF CATALYSIS, 2002, 23 (04) :295-296
12345