Preparation and properties of thermoplastic polyurethane-polylactic acid blends

被引：0

作者：

Zhao C. ^{[1
]}

Xu Y. ^{[1
]}

Wang C. ^{[1
]}

机构：

[1] Key Laboratory of Eco-Textiles, College of Textiles and Clothing, Jiangnan University, Wuxi

来源：

Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2017年 / 34卷 / 09期

关键词：

Blends; Melting blends; Polylactic acid; Thermal properties; Thermoplastic polyurethane;

D O I：

10.13801/j.cnki.fhclxb.20170220.001

中图分类号：

学科分类号：

摘要：

Various mass ratio thermoplastic polyurethane-polylactic acid (TPU-PLA) blends were prepared by melting blends. The morphology, thermal characteristics, and high-temperature processing performance of TPU-PLA blends were studied with SEM, DSC, TG, Vicat Softening Temperature (VST) and Melt Flow Rate (MFR), respectively. The results show that the morphologies of TPU and PLA in blends present as a “sea-island” distribution. Glass transition temperature Tg of the PLA in the blends changes from 69.60℃(Original PLA) to 57.58℃(PLA70), 53.29℃(PLA50) and 55.64℃(PLA30), and TPU distributes in PLA evenly as dispersing phases. There are clear interfaces between the dispersing phases and continuous phases. It indicates that TPU-PLA blends are an incompatible system. The crystallinity of original PLA is lower than that in TPU-PLA blends, due to overlapping of crystallization and melting. The initial decomposition temperature of TPU-PLA blends are around 180-200℃ and the fastest decomposition temperature of TPU-PLA are about 310-350℃. The thermal properties of TPU-PLA blends are favorable. When the mass ratio of TPU is 10%-30%, the material critical deformation temperature of blends is enhanced relatively to original PLA and TPU. The melt index of blends is increased firstly and then decreased as the mass ratio of TPU increased. As the mass ratio of TPU is 40%, the melting index of blends is highest which is 1406 g·(10 min)-1. © 2017, Chinese Society for Composite Materials. All right reserved.

引用

页码：2030 / 2037

页数：7

共 16 条

[1]

Diao H.X., The properties and preparation of PLA composites, (2011)

[2]

Mano J.F., Structural evolution of the amorphous phase during crystallization of poly(L-lactic acid): A synchrotron wide-angle X-ray scattering study, Journal of Non-Crystalline Solids, 353, 26, pp. 2567-2572, (2007)

[3]

Abe H., Takahashi N., Kim K.J., Et al., Thermal degradation processes of end-capped poly(L-lactide)s in the presence and absence of residual zinc catalyst, Biomacromolecules, 5, 4, pp. 1606-1614, (2004)

[4]

Chen Y., Luo L.F., Zeng G.S., Et al., Preparation and properties of PLA-g-GMA/Ope-POSS/PLA composites, Acta Materiae Compositae Sinica, 33, 1, pp. 61-70, (2016)

[5]

Li M., Li Y.F., The research progress of toughening modified polylactic acid, Acetaldehyde Acetate Chemical, 5, pp. 25-28, (2016)

[6]

Wang C.C., Li M.Q., Lei W., Research progress on 3D printing polylactic acid and its composites, Plastics Science and Technology, 44, 6, pp. 89-91, (2016)

[7]

Yu J., Han J., Zhu J.J., Et al., Structures and properties of fully biodegradable PLA/PBAT/PHBV blends, Acta Materiae Compositae Sinica, 33, 8, pp. 1608-1614, (2016)

[8]

Xu C.H., Crystallization behavior investigation of polylactide/poly (ethylene oxide) composites, Guangdong Chemical Industry, 39, 6, pp. 68-70, (2012)

[9]

Hao X., Kaschta J., Liu X., Et al., Entanglement network formed in miscible PLA/PMMA blends and its role in rheological and thermo-mechanical properties of the blends, Polymer, 80, pp. 38-45, (2015)

[10]

Ou Z.X., Zheng Y.Y., Xiao D.S., Et al., Preparation and properties of functional modification reduced graphene oxide-carbon nanotubes/thermoplastic polyurethane composite films, Acta Materiae Compositae Sinica, 33, 3, pp. 486-494, (2016)

← 1 2 →