Effect of chloride ion on stress corrosion crack growth rate of 316L stainless steel in high temperature pure water

被引：0

作者：

Lu, Hui ^{[1
]}

Du, Dong-Hai ^{[1
]}

Chen, Kai ^{[1
]}

Zhang, Le-Fu ^{[1
]}

机构：

[1] School of Nuclear Science and Engineering, Shanghai Jiao Tong University, Shanghai,200240, China

来源：

Yuanzineng Kexue Jishu/Atomic Energy Science and Technology | 2015年 / 49卷 / 10期

关键词：

D O I：

10.7538/yzk.2015.49.10.1849

中图分类号：

学科分类号：

摘要：

Drops - Steel corrosion - Growth rate - Austenitic stainless steel - Dissolved oxygen - High temperature corrosion - Chlorine compounds - Cracks - Ions - Nuclear fuels - Residual stresses - Nuclear power plants

引用

页码：1849 / 1854

共 3 条

[1] EFFECT OF PRESTRAIN ON STRESS-CORROSION CRACKING OF TYPE-304 STAINLESS-STEEL IN HIGH-TEMPERATURE WATER
KUNIYA, J
MASAOKA, I
SASAKI, R
NAKAGAWA, Y
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (06) : 442 - 447
[2] INFLUENCES OF STRESS RATIOS ON CYCLIC STRESS-CORROSION CRACK GROWTH-CHARACTERISTICS OF A HIGH-STRENGTH STEEL
ENDO, K
KOMAI, K
MATSUDA, Y
BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1981, 24 (197): : 1885 - 1892
[3] STRESS CORROSION CRACKING OF Cu-Zn-Al ALLOYS IN PURE STEAM AND WATER AT HIGH TEMPERATURE.
Sato, Shiro
Nagata, Koji
Sumitomo Light Metal Technical Reports, 1974, 15 (02): : 1 - 16

← 1 →