Weldability of 9Cr-ODS and JLF-1 Steels for Dissimilar Joining with Hot Isostatic Pressing and Electron Beam Welding*)

被引:0
作者
Fu, Haiying [1 ]
Nagasaka, Takuya [1 ,2 ]
Muroga, Takeo [1 ,2 ]
Guan, Wenhai [3 ]
Nogami, Shuhei [3 ]
Hasegawa, Akira [3 ]
Serizawa, Hisashi [4 ]
机构
[1] SOKENDAI (The Graduate University for Advanced Studies), 322-6 Oroshi-cho, Toki
[2] National Institute for Fusion Science, 322-6 Oroshi-cho, Toki
[3] Tohoku University, 6-6-01-2 Aramaki-aza-Aoba, Aoba-ku, 980-8578, Sendai
[4] Joining and Welding Research Institute, Osaka University, 11-1 Mihogaoka, Ibaraki
关键词
electron beam welding; hot isostatic pressing; joining strength; post-weld heat treatment;
D O I
10.1585/pfr.10.3405015
中图分类号
学科分类号
摘要
Dissimilar joints between 9Cr-ODS and JLF-1 were fabricated by hot isostatic pressing (HIP) and by electron beam welding (EBW), respectively. Compared to the HIP at 1000◦C, HIP at higher temperatures of 1050◦C and 1100◦C is effective to improve the joining strength of the joints. All the as-HIPed joints fractured at the interface during tensile tests. 1050◦C-HIP showed the best joining strength and reduction of area. Post-weld heat treatment (PWHT) with normalization and tempering (N&T) could further improve the joining properties of the HIPed joints. The joints fractured outside the interface at the JLF-1 base metals. EBW showed better weld-ability than HIP, because the joint made by EBW did not fracture at the weld metal during tensile tests, but always fractured at JLF-1 side. However, the properties of the HIPed joints were improved after PWHT with N&T, and were comparable to that made by EBW. © 2015 The Japan Society of Plasma Science and Nuclear Fusion Research
引用
收藏
页码:1 / 4
页数:3
相关论文
共 11 条
[1]  
Ukai S., Comprehensive Nuclear Materials, pp. 241-271, (2012)
[2]  
Tanno T., Ohtsuka S., Yano Y., Kaito T., Oba Y., Ohnuma M., Koyama S., Tanaka K., J. Nucl. Mater, 440, (2013)
[3]  
Li Y., Nagasaka T., Muroga T., Kimura A., Ukai S., Fusion Eng. Des, 86, (2011)
[4]  
Ukai S., Fujiwara M., J. Nucl. Mater, pp. 307-311, (2002)
[5]  
Hoelzer D.T., Unocic K.A., Sokolov M.A., Feng Z., J. Nucl. Mater, 442, (2013)
[6]  
Uwaba T., Ukai S., Nakai T., Fujiwara M., J. Nucl. Mater, pp. 367-370, (2007)
[7]  
Noh S., Kim B., Kasada R., Kimura A., J. Nucl. Mater, 426, (2012)
[8]  
Fu H.Y., Nagasaka T., Muroga T., Kimura A., Chen J.M., Fusion Eng. Des, 89, (2014)
[9]  
Commin L., Rieth M., Widak V., Dafferner B., Heger S., Zimmermann H., Materna-Morris E., Lindau R., J. Nucl. Mater, 442, (2013)
[10]  
Lindau R., Klimenkov M., Jantsch U., Moslang A., Commin L., J. Nucl. Mater, 416, (2011)