Effects of Ce, Cr and Er doping and annealing conditions on the microstructural features and electrical properties of PbZrO3 thin films prepared by sol-gel process

被引：24

作者：

Mensur Alkoy, Ebru ^{[1
,2
]}

Alkoy, Sedat ^{[1
,3
]}

Shiosaki, Tadashi ^{[1
]}

机构：

[1] Graduate School of Materials Science, Nara Institute of Science and Technology, Ikoma

[2] Department of Physics, Kocaeli University, 41300 Izmit, Kocaeli

[3] Electronic Materials Laboratory, Department of Materials Science and Engineering, Cebze Institute of Technology, 41400 Gebze, Kocaeli

来源：

Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers | 2005年 / 44卷 / 9 A期

关键词：

Antiferroelectrics; Doping; PbZrO[!sub]3[!/sub; Sol-gel; Thin films;

D O I：

10.1143/JJAP.44.6654

中图分类号：

学科分类号：

摘要：

Lead zirconate (PbZrO3) thin films doped with Ce, Cr and Er were grown on Pt(111)/Ti/SiO2/Si(100) substrates by sol-gel spin coating process. Polycrystalline films with a phase-pure perovskite structure and a random orientation were obtained regardless of doping materials. Microstructural examinations of the films revealed a two-phase microstructure consisting of large rosette-type perovskite regions with a nanocrystalline phase located in between. Perovskite rosettes were found to be of polycrystalline in nature with grain size ranging between 50-250 nm. Increasing number of annealing cycles and temperature were found to improve the microstructure, crystallinity and electrical properties. Doping elements were also found to increase electrical properties with a saturation polarization (Psat) reaching 65 × 10-6C/cm2 in Ce- and Cr-doped coatings compared to 39 × 10-6 C/cm2 for undoped PZ films. © 2005 The Japan Society of Applied Physics.

引用

页码：6654 / 6660

页数：6

共 15 条

[11] Wang Z.J., Maeda R., Ichiki M., Kokawa H., Jpn. J. Appl. Phys., 40, (2001)
[12] Wang Z.J., Aoki Y., Yan L.J., Kokawa H., Maeda R., J. Cryst. Growth, 267, (2004)
[13] Es-Souni M., Piorra A., Mater. Res. Bull., 36, (2001)
[14] Es-Souni M., Abed M., Solterbeck C.-H., Piorra A., Mater. Sci. Eng. B, 94, (2002)
[15] Moulson A.J., Herbert J.M., Electroceramics, (1990)

← 1 2 →