Influence of basicity and Fe2O3 on crystallisation characteristics of CaO-MgO-SiO2-Al2O3-Cr2O3-Fe2O3 system

被引：1
|
作者：
Wu, X.R. [1 ,2 ]
Wang, R.T. [1 ]
Lü, H.H. [1 ,2 ]
Shen, X.M. [1 ,2 ]
Li, L.S. [1 ,2 ]
机构：
[1] Anhui Provincial Key Lab of Metallurgical Engineering and Resources Recycling, Anhui University of Technology, Ma'anshan
[2] Key Laboratory of Metallurgical Emission Reduction and Resources Recycling, Ministry of Education, Anhui University of Technology, Ma'anshan
来源：
Materials Research Innovations | 2015年 / 19卷
关键词：
Basicity; Chromium oxide; Crystallisation; Spinel solid solution;
D O I：
10.1179/1432891715Z.0000000002191
中图分类号：
学科分类号：
摘要：
CaO-MgO-SiO2-Al2O3-Cr2O3-Fe2O3 slag systems with different basicities and different Fe2O3 contents were prepared using reagent powders and experimented cooling from melt to 1400°C for crystallisation. X-ray diffraction, Scanning Electronic Microscopy and Energy Dispersive Spectrometer were used for slag sample characterisation. It was established that the basicity of the slag changed the mineralogical phases, while variation of Fe2O3 content in slag with the same basicity did not affect the main crystalline phases. The results showed that most of the Cr2O3 was incorporated into Mg(Al,Fe,Cr)2O4 spinel solid solution and content of Cr2O3 in spinel phase decreased with increasing of the basicity (CaO/SiO2) and the Fe2O3 content. © 2015 W. S. Maney & Son Ltd.
引用
收藏
页码：345 / 349
页数：4
相关论文
共 50 条
  • [21] Effects of the Cr2O3 Content on the Viscosity of CaO-SiO2-10 Pct Al2O3-Cr2O3 Quaternary Slag
    Wu, Tuo
    Zhang, Yanling
    Yuan, Fang
    An, Zhuoqing
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2018, 49 (04): : 1719 - 1731
  • [22] New insights on consolidation behavior of Fe2O3 in the Fe3O4-CaO-MgO-SiO2 system for fluxed pellet production: Phase transformations and morphology evolution
    Shi, Shurong
    Gao, Lihua
    Zhang, Junhong
    He, Zhijun
    MINERALS ENGINEERING, 2024, 214
  • [23] Phase Equilibria Studies in the CaO-MgO-Al2O3-SiO2 System with Al2O3/SiO2 Weight Ratio of 0.4
    Liao, Jinfa
    Qing, Gele
    Zhao, Baojun
    METALS, 2023, 13 (02)
  • [24] Calculation model of mass action concentrations for CaO-MgO-SiO2-Al2O3-Cr2O3 penta-slag
    Guo, Hua
    Hu, Yu Ting
    Cang, Da Qiang
    Jin, Yi
    Wang, Li Xin
    Cheng, Xiang Li
    Bai, Hao
    Zong, Yan Bing
    CHINESE CHEMICAL LETTERS, 2010, 21 (02) : 229 - 233
  • [25] Metallurgical properties of CaO-SiO2-Al2O3-4.6wt%MgO-Fe2O3 slag system pertaining to spent automotive catalyst smelting
    Zheng, Ruili
    Lu, Jianfang
    Song, Weifeng
    Liu, Mudan
    Li, Huashan
    Liu, Yong
    Lu, Xianjin
    Ma, Zhiyuan
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2023, 30 (05) : 886 - 896
  • [26] Effects of Al2O3, Fe2O3, and SiO2 on Cr(VI) formation during heating of solid waste containing Cr(III)
    Mao, Linqiang
    Deng, Ning
    Liu, Lu
    Cui, Hao
    Zhang, Wenyi
    CHEMICAL ENGINEERING JOURNAL, 2016, 304 : 216 - 222
  • [27] Phosphate enrichment mechanism in CaO–SiO2–FeO–Fe2O3–P2O5 steelmaking slags with lower binary basicity
    Jin-yan Li
    Mei Zhang
    Min Guo
    Xue-min Yang
    International Journal of Minerals Metallurgy and Materials, 2016, 23 (05) : 520 - 533
  • [28] Phosphate enrichment mechanism in CaO–SiO2–FeO–Fe2O3–P2O5 steelmaking slags with lower binary basicity
    Jin-yan Li
    Mei Zhang
    Min Guo
    Xue-min Yang
    International Journal of Minerals, Metallurgy, and Materials, 2016, 23 : 520 - 533
  • [29] Solubility Measurements of Fe2O3 and Cr2O3 in Fused Na2B4O7-B2O3 in Air at 1173 K
    Toki, Ryutaro
    Doi, Takashi
    Otsuka, Nobuo
    MATERIALS TRANSACTIONS, 2016, 57 (02) : 143 - 147
  • [30] Dissolution Kinetics of Synthetic FeCr2O4 in CaO-MgO-Al2O3-SiO2 Slag
    Wei, Kangji
    Wang, Lijun
    Liu, Shiyuan
    He, Xiaobo
    Xiao, Yiyu
    Chou, Kuochih
    ISIJ INTERNATIONAL, 2022, 62 (04) : 617 - 625
12345