Influence of basicity and Fe2O3 on crystallisation characteristics of CaO-MgO-SiO2-Al2O3-Cr2O3-Fe2O3 system

被引：1
|
作者：
Wu, X.R. [1 ,2 ]
Wang, R.T. [1 ]
Lü, H.H. [1 ,2 ]
Shen, X.M. [1 ,2 ]
Li, L.S. [1 ,2 ]
机构：
[1] Anhui Provincial Key Lab of Metallurgical Engineering and Resources Recycling, Anhui University of Technology, Ma'anshan
[2] Key Laboratory of Metallurgical Emission Reduction and Resources Recycling, Ministry of Education, Anhui University of Technology, Ma'anshan
来源：
Materials Research Innovations | 2015年 / 19卷
关键词：
Basicity; Chromium oxide; Crystallisation; Spinel solid solution;
D O I：
10.1179/1432891715Z.0000000002191
中图分类号：
学科分类号：
摘要：
CaO-MgO-SiO2-Al2O3-Cr2O3-Fe2O3 slag systems with different basicities and different Fe2O3 contents were prepared using reagent powders and experimented cooling from melt to 1400°C for crystallisation. X-ray diffraction, Scanning Electronic Microscopy and Energy Dispersive Spectrometer were used for slag sample characterisation. It was established that the basicity of the slag changed the mineralogical phases, while variation of Fe2O3 content in slag with the same basicity did not affect the main crystalline phases. The results showed that most of the Cr2O3 was incorporated into Mg(Al,Fe,Cr)2O4 spinel solid solution and content of Cr2O3 in spinel phase decreased with increasing of the basicity (CaO/SiO2) and the Fe2O3 content. © 2015 W. S. Maney & Son Ltd.
引用
收藏
页码：345 / 349
页数：4
相关论文
共 50 条
  • [11] Effects of MgO, Na2O, and B2O3 on the Viscosity and Structure of Cr2O3-bearing CaO-SiO2-Al2O3 Slags
    Li, Qiuhan
    Yang, Shufeng
    Zhang, Yanling
    An, Zhuoqing
    Guo, Zhancheng
    ISIJ INTERNATIONAL, 2017, 57 (04) : 689 - 696
  • [12] Effect of MgO/Al2O3 and CaO/SiO2 on the Metallurgical Properties of CaO-SiO2-Al2O3-MgO-TiO2 Slag
    Qiu, Guo-xing
    Miao, De-jun
    Wei, Xu-li
    Bai, Chong
    Li, Xiao-ming
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2022, 585
  • [13] Effect of TiO2 on reduction behavior of Cr2O3 in CaO–SiO2–Al2O3–MgO–TiO2–Cr2O3 by carbon from Fe–C melt
    Jun-yi Xiang
    Gui-shang Pei
    Wei Lv
    Bao-hua Li
    Gui-bao Qiu
    Xue-wei Lv
    Journal of Iron and Steel Research International, 2020, 27 : 1145 - 1152
  • [14] Influence of B2O3 and Basicity of CaO–SiO2–B2O3–Al2O3 Slag on the Saturation Concentration of Magnesium Oxide
    Babenko A.A.
    Smetannikov A.N.
    Zhuchkov V.I.
    Upolovnikova A.G.
    Steel in Translation, 2019, 49 (02) : 87 - 90
  • [15] Viscosity Measurement and Structure Analysis of Cr2O3-Bearing CaO-SiO2-MgO-Al2O3 Slags
    Li, Qiuhan
    Gao, Jintao
    Zhang, Yanling
    An, Zhuoqing
    Guo, Zhancheng
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2017, 48 (01): : 346 - 356
  • [16] Carbothermic reduction of Cr2O3 and Fe2O3 under nonisothermal condition
    Okumura, K
    Sugimura, T
    Kuwabara, M
    Sano, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2004, 90 (12): : 992 - 998
  • [17] Measurements of the Solubility of Fe2O3 and Cr2O3 in Fused Na2O-B2O3 Salts at 1173 K
    Toki, Ryutaro
    Doi, Takashi
    Otsuka, Nobuo
    JOURNAL OF THE JAPAN INSTITUTE OF METALS AND MATERIALS, 2014, 78 (10) : 395 - 399
  • [18] Interaction of yttria stabilized zirconia electrolyte with Fe2O3 and Cr2O3
    Molin, Sebastian
    Gazda, Maria
    Jasinski, Piotr
    JOURNAL OF POWER SOURCES, 2009, 194 (01) : 20 - 24
  • [19] Study of structure and optical properties of Fe2O3•CaO•Bi2O3 glasses
    Sanghi, Sujata
    Duhan, Sarita
    Agarwal, Ashish
    Aghamkar, Praveen
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 488 (01) : 454 - 458
  • [20] Effects of Basicity on the Phase Composition, Structure, Viscosity, and Crystallization Temperature of CaO-SiO2-Al2O3-MgO-B2O3 Slags
    Babenko, A. A.
    Shartdinov, R. R.
    Upolovnikova, A. G.
    Smetannikov, A. N.
    METALLURGIST, 2023, 67 (1-2) : 166 - 175
12345