Laser power effect on microstructure and property of laser cladding nickel based alloy coating

被引：0
|
作者：
Deng D. [1 ,2 ]
Sun J. [1 ]
Wang X. [1 ]
Zhang H. [1 ]
机构：
[1] Faculty of Mechanical Engineering, Materials and Energy, Dalian University of Technology, Dalian
[2] R&D Division of Shenyang Blower Works Group Corporation, Shenyang
来源：
Xiyou Jinshu/Chinese Journal of Rare Metals | 2016年 / 40卷 / 01期
关键词：
Laser cladding; Laser power; Nickel-based alloy;
D O I：
10.13373/j.cnki.cjrm.2016.01.004
中图分类号：
学科分类号：
摘要：
As to the cavitation that occurred in the high boron solution working medium for water-lubricated guiding bearing, the method of laser cladding was proposed to improve their surface properties. Ni40 alloy powder was cladded on the surface of 304 austenitic stainless steel by laser cladding, and then the effect of laser power on the microstructure and properties of the cladding layer was studied. 304 austenitic stainless steel was cladded by semiconductor laser, and a cladding layer with thickness of 0.8 mm was formed. The microstructure of samples was analyzed by optical microscopy(OM) and scanning electron microscopy(SEM), the cross-sectional hardness gradient of the cladding was measured by Vickers hardness, the abrasion of cladding layer was tested by wear testing machine, and the corrosion resistance testing was carried out in solution of boric acid. The experience results showed that Ni40 cladding layer was mainly composed of γ-Ni and chromium compounds. The different laser powers used in the experiment had influence on the structure size of the cladding layer and element distribution, but no influence on the phase constitution. Compared with the substrate, the hardness of cladding layer increased significantly and decreased with the laser power increasing. The thickness of cladding layer increased with the laser power increasing. During the friction and the wear process, the wear mass loss of cladding layer was about 1.5×10-2 g and declined with laser power increasing. And the corrosion resistance of cladding layer rose with the increase of laser power in the boric acid solution. © Editorial Office of Chinese Journal of Rare Metals. All right reserved.
引用
收藏
页码：20 / 25
页数：5
相关论文
共 17 条
  • [1] Zhang L., Zhou Q., Chu Z.H., Analysis of one million kilowatts PWR containment spray pumps, General Machinery, 2, (2012)
  • [2] Vilar R., Laser cladding, Journal of Laser Applications, 11, 2, (1999)
  • [3] Wang Y.B., Wear and Corrosion Coatings Prepared by Laser Cladding, (2009)
  • [4] Zuo T.C., Chen H., 21st century green manufacturing-technology and application of laser manufacturing, Journal of Mechanical Engineering, 45, 10, (2009)
  • [5] Xu R.H., Li X.F., Zuo D.W., Wang H.Y., Jiang S.H., Li J.Z., Microstructure and hardness of NiCoCrAlY coatings on titanium alloy by laser cladding with different scanning speeds, Chinese Journal of Rare Metals, 38, 5, (2014)
  • [6] Wu D.J., Chen Y.X., Lu W.F., Ma G.Y., Guo Y.Q., Guo D.M., Dilution characteristics of mutual melting of Al<sub>2</sub>O<sub>3</sub>-13% TiO<sub>2</sub> coating on the surface of titanium alloy by laser cladding, Rare Metal Materials and Engineering, 41, 12, (2012)
  • [7] Wu Y., Yu G., He X.L., Ning J.W., The structure and high-temperature ablation aerodynamic performance of Ta-W alloy by laser cladding, Rare Metal Materials and Engineering, 41, 7, (2012)
  • [8] Qiu X.W., Zhang Y.P., Liu C.G., Wear resistance of Ni-base alloy by laser cladding, Rare Metal Materials and Engineering, 41, 2, (2012)
  • [9] Zhang X.W., Liu H.X., Jiang Y.H., Wang C.Q., Zeng W.H., Advances in functional composite coating by laser cladding Ti<sub>6</sub>Al<sub>4</sub>V alloy, Rare Metal Materials and Engineering, 41, 1, (2012)
  • [10] Hemmati I., Ocelik D., Hosson J.T.M., Advances in laser surface engineering: tackling the cracking problem in laser-deposited Ni-Cr-B-Si-C alloys, Advances in Laser Surface Engineering, 65, 6, (2013)
12