Influence of powder morphology and sintering temperature on the properties of hydroxyapatite

被引：0

作者：

Kelvin Chew, W.J. ^{[1
]}

Niakan, A. ^{[2
]}

Nawawi, N.A. ^{[2
]}

Bang, L.T. ^{[2
]}

Ramesh, S. ^{[2
]}

机构：

[1] School of Engineering, Taylor's University, Taylor's Lakeside Campus, No. 1 Jalan Taylor's, Subang Jaya

[2] Center of Advanced Manufacturing and Material Processing, Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur

来源：

International Journal of Automotive and Mechanical Engineering | 2015年 / 12卷

关键词：

Bioceramics; Decomposition; Hydroxyapatite (HA); Morphology;

D O I：

10.15282/IJAME.12.2015.22.0257

中图分类号：

学科分类号：

摘要：

The effect of sintering two hydroxyapatite (HA) powders (designated HAC and HAS) of contrasting morphology, at temperatures ranging from 1000°C to 1450°C, on the phase stability of the material was investigated. Pellets were prepared by cold isostatic pressing of the powders at 200 MPa and subsequently sintering in air at a heating rate of 2°C/min. and a holding time of 2 hours. X-ray diffraction analysis revealed that decomposition of the HA was dependent on the morphology of the precursor powders. The decomposition of the HAS powder started to occur at a lower sintering temperature of 1300°C, whereas the HAC powder only decomposes at 1400°C. Both powders formed residual phases of tri-calcium phosphates and tetra-calcium phosphate due to decomposition. The possible factors controlling the decomposition mechanism of the HA powders are also discussed. © Universiti Malaysia Pahang.

引用

页码：3089 / 3096

页数：7

共 50 条

[41] Sintering effect on the microstructural, mechanical, and in vitro bioactivity properties of a commercially synthetic hydroxyapatite [J].

Pazarlioglu, Serdar ;

Salman, Serdar .

JOURNAL OF THE AUSTRALIAN CERAMIC SOCIETY, 2017, 53 (02) :391-401

[42] Influence of drying air temperature and carrier agent concentration on the physicochemical properties of acai juice powder [J].

Tonon, Renata Valeriano ;

Brabet, Catherine ;

Hubinger, Miriam Dupas .

CIENCIA E TECNOLOGIA DE ALIMENTOS, 2009, 29 (02) :444-450

[43] Development of Triphasic Hydroxyapatite/(α and β)-Tricalcium Phosphate Based Composites by Sintering Powder of Calcium-Apatite in the Presence of Montmorillonite [J].

Jamil, M. ;

Elouahli, A. ;

Abida, F. ;

Khallok, H. ;

Gourri, E. ;

Kheribech, A. ;

Hatim, Z. .

JOURNAL OF INORGANIC AND ORGANOMETALLIC POLYMERS AND MATERIALS, 2020, 30 (07) :2489-2498

[44] Morphology and Properties of Antheraea Pernyi silk Fibroin/hydroxyapatite Composite Films [J].

Zhang Wei ;

Tian Hui-min .

2011 INTERNATIONAL FORUM ON BIOMEDICAL TEXTILE MATERIALS, PROCEEDINGS, 2011, :42-44

[45] Can porosity influence the osteoconductive properties of synthetic hydroxyapatite? [J].

Specchia, N ;

Pagnotta, A ;

Greco, F .

BIOCERAMICS, 2000, 192-1 :355-358

[46] Influence of hydrothermal synthesis parameters on the properties of hydroxyapatite nanoparticles [J].

Kusnieruk, Sylwia ;

Wojnarowicz, Jacek ;

Chodara, Agnieszka ;

Chudoba, Tadeusz ;

Gierlotka, Stanislaw ;

Lojkowski, Witold .

BEILSTEIN JOURNAL OF NANOTECHNOLOGY, 2016, 7 :1586-1601

[47] Influence of Barium Hexaferrite on Magnetic Properties of Hydroxyapatite Ceramics [J].

Jarupoom, P. ;

Jaita, P. .

JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2015, 15 (11) :9217-9221

[48] Consolidation of nanocrystalline hydroxyapatite powder [J].

Ramesh, S. ;

Tan, C. Y. ;

Sopyan, I. ;

Hamdi, M. ;

Teng, W. D. .

SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2007, 8 (1-2) :124-130

[49] EFFECT OF CALCINATION ON THE SINTERING BEHAVIOUR OF HYDROXYAPATITE [J].

Teh, Y. C. ;

Tan, C. Y. ;

Ramesh, S. ;

Purbolaksono, J. ;

Tan, Y. M. ;

Chandran, Hari ;

Teng, W. D. ;

Yap, B. K. .

CERAMICS-SILIKATY, 2014, 58 (04) :320-325

[50] Effect of High Temperature on Morphology and Structure of Nano-hydroxyapatite/collagen Composite [J].

Song, Qiang ;

Hu, Kun ;

Cui, Fuzhai ;

He, Zhouying .

MATERIALS RESEARCH, PTS 1 AND 2, 2009, 610-613 :1360-1363

← 1 2 3 4 5 →