The mechanisms of cavitation erosion of the Elektron21 magnesium alloy

被引：3

作者：

Silesian University of Technology, ul. Krasińskiego 8, Katowice ^{[1
]}

40-019, Poland

不详 ^{[2
]}

20-618, Poland

机构：

[1] Silesian University of Technology, ul. Krasińskiego 8, Katowice

[2] Lublin University of Technology, ul. Nadbystrzycka 36, Lublin

来源：

Solid State Phenomena | / 99-104期

关键词：

Cavitation; Degradation mechanisms; Elektron21 Mg alloy; Microstructure; SEM;

D O I：

10.4028/www.scientific.net/SSP.229.99

中图分类号：

学科分类号：

摘要：

Magnesium and its alloys may be applied as cathodic protection for steel constructions. As the protectors work in water environment, one of the main degradation factors is cavitation erosion. The paper presents results of research on the cavitation erosion of magnesium casting alloy -Elektron 21. The cavitation erosion tests were performed using vibratory apparatus. After the cavitation tests eroded surface and the cross-sections of the specimens were observed by means of scanning electron microscopy. Elektron 21 did not exhibit distinct incubation period of cavitation erosion. The cavitation pits are observed mainly in the α-Mg solid solution grains and on the interfaces between intermetallic phases and the α-Mg. On the other hand, the Mg3(Nd, Gd) eutectic phases are more resistant to cavitation erosion than α-Mg. They are protecting the solid solution from degradation. However, due to their high hardness they undergo cracking and detachment of from the surface. After longer times of cavitation tests, cracks begin to propagate into the material, which leads to crushing of bigger parts of the material. © (2015) Trans Tech Publications, Switzerland.

引用

页码：99 / 104

页数：5

共 11 条

[1]

Kielbus A., Rzychon T., The intermetallic phases in sand casting magnesium alloys for elevated temperature, Materials Science Forum, 690, pp. 214-217, (2011)

[2]

Fontana M.G., (2005)

[3]

Adamiec J., Weldability of Magnesium Alloys, (2010)

[4]

Zeng R., Dietzel W., Witte F., Hort N., Blawert C., Progress and challenge for magnesium alloys as biomaterials, Advanced Biomaterials, 10, pp. BB3-B14, (2008)

[5]

Jasionowski R., Przetakiewicz D., Przetakiewicz W., Cavitation Erosion Resistance of Alloys Used in Cathodic Protection of Hulls of Ships, Amm, 59, pp. 241-245, (2014)

[6]

Feller H.G., Kharrazi Y., Cavitation erosion of metals and alloys, Wear, 93, pp. 249-260, (1984)

[7]

Richman R.H., McNaughton W.P., Correlation of cavitation erosion behavior with mechanical properties of metals, Wear, 140, pp. 63-82, (1990)

[8]

ASTM International, (1998)

[9]

Szala M., Hejwowski T., Lenart I., Cavitation erosion resistance of Ni-Co based coatings, Advances in Science and Technology -Research Journal, 8, pp. 36-42, (2014)

[10]

Franc J.P., Michel J.M., Fundamentals of Cavitation, (2011)

← 1 2 →